316L不锈钢化学成分
| 化学成分/% | |||||||||||
| 牌号 | C | Si | Mn | P | S | Ni | Cr | Mo | Cu | N | 其他 |
| 316 | ≤0.07 | ≤1.0 | 2.00 | ≤0.035 | ≤0.03 | 10.00~14.00 | 16.0~18.0 | 2.00-3.00 | — | — | |
| 316L | ≤0.03 | ≤1.00 | ≤2.00 | ≤0.035 | ≤0.03 | 10.0-14.0 | 16.0-18.0 | 2.0-3.0 | — | — | |
316L不锈钢力学性能
| 牌号 | 热处理 | 屈服强度σ0.2/Mpa | 抗拉强度σb/Mpa | 伸长率δ5/% | HBS | HRB | HV |
| 316 | 1010~1120快冷 | ≥205 | ≥520 | ≥40 | ≤187 | ≤90 | ≤200 |
| 316L | 1010~1150C。 | ≥175 | ≥480 | ≥40 | ≤187 | ≤90 | ≤200
|