Celanese Celcon® M90™ POM, Unfilled 物性表
| 比重 | 1.41 g/cc | 1.41 g/cc | ASTM D792 |
| 密度 | 1.41 g/cc | 0.0509 lb/in³ | ISO 1183 |
| Density of Compound | 1.20 g/cc | 0.0434 lb/in³ | |
| 水分吸收 | 0.200 % | 0.200 % | 23°C/50%RH; ISO 62 |
| 饱和吸水率 | 0.750 % | 0.750 % | ISO 62 |
| 线性成型收缩率,Flow | 0.0200 cm/cm | 0.0200 in/in | ISO 294-4 |
| 0.0220 cm/cm | 0.0220 in/in | ASTM D955 | |
| 线性成型收缩率，横向 | 0.0180 cm/cm | 0.0180 in/in | ASTM D955 |
| 0.0190 cm/cm | 0.0190 in/in | ISO 294-4 | |
| 熔体流动速率 | 9.00 g/10 min | 9.00 g/10 min | ASTM D1238 |
| 8.00 g/10 min @Load 2.16 kg, Temperature 190 °C | 8.00 g/10 min @Load 4.76 lb, Temperature 374 °F | [cm3/10min]; ISO 1133 |
| 抗张强度(屈服) | 60.7 MPa | 8800 psi | ASTM D638 |
| 66.0 MPa | 9570 psi | 50mm/min; ISO 527-2/1A | |
| 34.5 MPa @Temperature 71.1 °C | 5000 psi @Temperature 160 °F | ASTM D638 | |
| 94.5 MPa @Temperature -40.0 °C | 13700 psi @Temperature -40.0 °F | ASTM D638 | |
| 屈服伸长率 | 10.0 % | 10.0 % | 50mm/min; ISO 527-2/1A |
| 拉伸模量 | 2.76 GPa | 400 ksi | 50mm/min; ISO 527-2/1A |
| 弯曲模量 | 2.55 GPa | 370 ksi | ISO 178 |
| 2.59 GPa | 375 ksi | ASTM D790 | |
| 0.689 GPa @Temperature 104 °C | 100 ksi @Temperature 220 °F | ASTM D790 | |
| 1.24 GPa @Temperature 71.1 °C | 180 ksi @Temperature 160 °F | ASTM D790 | |
| 悬壁梁缺口冲击强度 | 0.694 J/cm | 1.30 ft-lb/in | ASTM D256 |
| 0.534 J/cm @Temperature -40.0 °C | 1.00 ft-lb/in @Temperature -40.0 °F | ASTM D256 | |
| 5.70 kJ/m² | 2.71 ft-lb/in² | ISO 180/1A | |
| 简支梁无缺口冲击强度 | 18.8 J/cm² | 89.5 ft-lb/in² | ISO 179/1eU |
| 18.1 J/cm² @Temperature -30.0 °C | 86.1 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eU | |
| 简支梁缺口冲击强度 | 0.600 J/cm² | 2.86 ft-lb/in² | ISO 179/1eA |
| 0.600 J/cm² @Temperature -30.0 °C | 2.86 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eA | |
| 拉伸蠕变模量(1 hr) | 2450 MPa | 355000 psi | ISO 899-1 |
| 拉伸蠕变模量(1000 hr) | 1350 MPa | 196000 psi | ISO 899-1 |
| 体积电阻率 | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | ASTM D257 |
| 8.00e+14 ohm-cm | 8.00e+14 ohm-cm | IEC 60093 | |
| 表面电阻 | 3.00e+16 ohm | 3.00e+16 ohm | IEC 60093 |
| 线形热膨胀系数 - 流动 | 120 µm/m-°C | 66.7 µin/in-°F | ISO 11359-2 |
| 线性热膨胀系数,横向流动 | 120 µm/m-°C | 66.7 µin/in-°F | ISO 11359-2 |
| 比热容 | 2.21 J/g-°C | 0.528 BTU/lb-°F | |
| 导热系数 | 0.155 W/m-K | 1.08 BTU-in/hr-ft²-°F | |
| 熔融温度 | 165 °C | 329 °F | 10°C/min; ISO 11357-1,-2,-3 |
| 165 °C | 329 °F | ASTM D3418 | |
| 载荷下热变形温度(0.46 MPa) | 158 °C | 316 °F | ISO 75-1, -2 |
| 载荷下热变形温度(1.8 MPa) | 101 °C | 214 °F | ISO 75-1, -2 |
| 110 °C | 230 °F | ASTM D648 |
| 加工温度 | 80.0 - 120 °C | 176 - 248 °F | cavity |
| 180 - 200 °C | 356 - 392 °F | hot runner | |
| 1区 | 170 - 180 °C | 338 - 356 °F | |
| 2区 | 180 - 190 °C | 356 - 374 °F | |
| 3区 | 180 - 190 °C | 356 - 374 °F | |
| 4区 | 190 - 200 °C | 374 - 392 °F | |
| 模具温度 | 190 - 200 °C | 374 - 392 °F | |
| 加工（熔体）温度 | 180 - 200 °C | 356 - 392 °F | |
| Ejection Temperature | 140 °C | 284 °F | |
| 干燥温度 | 80.0 - 100 °C | 176 - 212 °F | |
| 干燥时间 | 3.00 hour | 3.00 hour | |
| 注射压力 | 60.0 - 120 MPa | 8700 - 17400 psi | |
| 保压 | 60.0 - 120 MPa | 8700 - 17400 psi | |
| 背压 | <= 4.00 MPa | <= 580 psi |
| Eff. thermal diffusivity | 4.85E-08 | [m^2/s] |
| 注塑 | Yes | |
| 射速 | slow-medium | |
| Pellets | Yes | |
| Processing conditions acc. ISO | 9988-2 | |
| Profile extrusion | Yes |