LUVOCOM® 1105-7310Polyetheretherketone
Lehmann & Voss & Co.
玻璃纤维增强材料
产品说明：
LUVOCOM® 1105-7310是一种聚醚醚酮(PEEK)材料,含有的填充物为玻璃纤维增强材料。 该产品在北美洲、非洲和中东、拉丁美洲、欧洲或亚太地区有供货,。
LUVOCOM® 1105-7310的主要特性有:
阻燃/额定火焰
Flame Retardant
具可灭菌性
抗翘曲
良好的尺寸稳定性
典型应用领域包括:
纺织/纤维
工程/工业配件
航空航天
汽车行业
医疗/保健
物性信息：
| 填料/增强材料 | 玻璃纤维增强材料 |
| 特性 | 尺寸稳定性良好 低翘曲性 良好的流动性 耐化学性良好 耐热性，高 耐水解性 用蒸汽消毒 阻燃性 |
| 用途 | 纺织应用 工程配件 航空航天应用 汽车领域的应用 医疗/护理用品 |
| 外观 | 自然色 |
| 密度 | 1.52 | g/cm³ | ISO 1183 |
| 熔流率（熔体流动速率） (380°C/5.0 kg) | 11 | g/10 min | ISO 1133 |
| 收缩率 | 0.40 到 0.90 | % | DIN 16901 |
| 吸水率 (23°C, 24 hr) | < 0.10 | % |
| 拉伸模量 | 6000 | MPa | ISO 527-2 |
| 拉伸应力 (断裂) | 85.0 | MPa | ISO 527-2 |
| 拉伸应变 (屈服) | 2.5 | % | ISO 527-2 |
| 弯曲模量 | 5000 | MPa | ISO 178 |
| 弯曲应力 | 125 | MPa | ISO 178 |
| 摩擦系数 | |||
| Dynamic | 0.32 | ||
| Static | 0.30 | ||
| Flexural Strain at Flexural Strength | 3.2 | % | ISO 178 |
| 最高使用温度 - Short Term | 260 | °C |
| 绝缘电阻 | > 1.0E+12 | ohms | IEC 60167 |
| 简支梁无缺口冲击强度 (23°C) | 40 | kJ/m² | ISO 179/1fU |
| 连续使用温度 | 250 | °C | UL 746B |
| 维卡软化温度 | 325 | °C | ISO 306/A |
| UL 阻燃等级 1 | V-0 | UL 94 |
| 干燥温度 | |||
| 热风干燥机, A | 150 | °C | |
| 热风干燥机, B | 120 | °C | |
| 干燥时间 | |||
| 热风干燥机, A | 3.0 到 6.0 | hr | |
| 热风干燥机, B | 6.0 到 8.0 | hr | |
| 建议的最大水分含量 | 0.050 | % | |
| 料筒后部温度 | 360 到 370 | °C | |
| 料筒中部温度 | 380 到 390 | °C | |
| 料筒前部温度 | 390 到 400 | °C | |
| 射嘴温度 | 360 到 380 | °C | |
| 加工（熔体）温度 | 390 | °C | |
| 模具温度 | 170 到 190 | °C |
| General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing, the moisture content should not exceed 0.05%. To avoid internal stresses, a medium to high injection rate should be used. An increase in tool temperature may be helpful. Post-crystallization may lead to warpage at elevated operating temperatures. This can be counteracted by suitable heat treatment. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. High-temperature polymers place increased demands on the tool steels employed. Please contact us for further information. |
| 1 . | Not recognized by UL. |