物性表

物性纠错

物性性能测试条件测试方法测试结果单位密度
ASTM D792/ISO 11831.14
吸水率 23℃/24H
ASTM D570/ISO 621.2%物理性能测试条件测试方法测试结果单位泰伯磨耗量1000g,CS-17ASTM D-10443.5%水｜-mg/1000次1000g,CS-17ASTM D-1044无水｜8mg/1000次收缩率MD：1.00mm3%0.80到1.5--MD：3.00mm4%1.5到2.2--吸水率23°C,24hr%1.2--饱和,23°C%8.0--机械性能测试条件测试方法测试结果单位拉伸应力-40°CMPa115
23°CMPa80.050.080°CMPa40.040.0拉伸应变屈服,23°C%1.5--断裂,23°C%25
弯曲模量-40°CMPa4300410023°CMPa2900140080°CMPa900500抗拉屈服强度23℃ASTM D-6383.5%水｜530kg/cm2压缩强度23℃ASTM D-695无水｜910kg/cm223℃ASTM D-6953.5%水｜-kg/cm2挠曲强度23℃ASTM D-790无水｜1150kg/cm223℃ASTM D-7903.5%水｜650kg/cm2抗拉屈服强度80℃ASTM D-638无水｜430kg/cm280℃ASTM D-6383.5%水｜400kg/cm2挠曲模量23℃ASTM D-7903.5%水｜14000kg/cm2抗拉屈服强度23℃ASTM D-638无水｜800kg/cm2挠曲模量-40℃ASTM D-790无水｜44000kg/cm2-40℃ASTM D-7903.5%水｜42000kg/cm2洛氏硬度23℃ASTM D-785无水｜97M-标度23℃ASTM D-7853.5%水｜-M-标度抗剪强度23℃ASTM D-732无水｜790kg/cm2挠曲强度-40℃ASTM D-7903.5%水｜1300kg/cm2断裂伸长率23℃ASTM D-638无水｜90%23℃ASTM D-6383.5%水｜< 200%弯曲强度
ASTM D790/ISO 1782.8kg·cm/cm(J/M)ft·lb/in抗剪强度23℃ASTM D-7323.5%水｜770kg/cm2挠曲强度80℃ASTM D-790无水｜640kg/cm280℃ASTM D-7903.5%水｜400kg/cm2挠曲模量80℃ASTM D-790无水｜9000kg/cm280℃ASTM D-7903.5%水｜5000kg/cm2洛氏硬度23℃ASTM D-785无水｜119R-标度23℃ASTM D-7853.5%水｜100R-标度挠曲模量23℃ASTM D-790无水｜29000kg/cm2弯曲应力-40°CMPa140
23°CMPa11565.080°CMPa65.040.0压缩应力23°CMPa90.0--剪切强度23°CMPa80.075.0泰伯耐磨性1000Cyclesmg8.00--摩擦系数-vs.metal5

0.15到0.20--抗拉屈服强度-40℃ASTM D-638无水｜1150kg/cm2-40℃ASTM D-6383.5%水｜1100kg/cm2挠曲强度-40℃ASTM D-790无水｜1450kg/cm2Charpy冲击强度
ASTM D256/ISO 17950kg·cm/cm(J/M)ft·lb/inIZOD冲击强度23℃，无缺口1/8
3.5%水｜-kg·cm/cm223℃，V缺口1/2ASTM D-256无水｜5kg·cm/cm23℃，V缺口1/2ASTM D-2563.5%水｜28kg·cm/cm-40℃，V缺口1/2ASTM D-256无水｜3.5kg·cm/cm-40℃，V缺口1/2ASTM D-2563.5%水｜-kg·cm/cm23℃，无缺口1/8
无水｜无断裂kg·cm/cm2热性能测试条件测试方法测试结果单位燃烧性（率）
UL94V-2
热变形温度
ASTM D648/ISO 75220(0.46MPa)℃（℉）线性膨胀系数
ASTM D696/ISO 113590.32mm/mm.℃热挠曲温度4.6kg/cm2ASTM D-648无水｜220°C4.6kg/cm2ASTM D-6483.5%水｜-°C熔点
差示扫描测热计DSC无水｜265°C
差示扫描测热计DSC3.5%水｜-°C比热

无水｜0.4Cal/g·℃

3.5%水｜-Cal/g·℃线性热膨胀系数
ASTM D-696无水｜9-10×10-5cm/cm/℃
ASTM D-6963.5%水｜-×10-5cm/cm/℃UL-94抗燃级1/32"UL 94无水｜V-2
1/32"UL 943.5%水｜-
导热系数

无水｜0.21Kcal/m·hr·℃

3.5%水｜-Kcal/m·hr·℃热变形温度0.45MPa,未退火°C220--熔融温度
°C265--线形热膨胀系数MDcm/cm/°C9.0E-5到1.0E-4--比热
J/kg/°C2100--导热系数
W/m/K0.32--电气性能测试条件测试方法测试结果单位体积电阻率
ohms·cm1.0E+13到1.0E+141.0E+12到1.0E+13介电常数623°C,50Hz
1.60--耗散因数623°C,50Hz
0.060--相比耐漏电起痕指数CTIV530--IEC导电径迹指数
UL 746无水｜-V
UL 7463.5%水｜530V介电常数50HzASTM D-150无水｜1.6
50HzASTM D-1503.5%水｜-
体积电阻率
ASTM D-257无水｜1014-1015Ω.cm介电常数
ASTM D150/IEC 602503.3
体积电阻率
ASTM D-2573.5%水｜1012-1013Ω.cm损耗因数50HzASTM D-150无水｜0.06
50HzASTM D-1503.5%水｜-
冲击性能测试条件测试方法测试结果单位简支梁无缺口冲击强度-40°C
无断裂--23°C
无断裂--
-40°CkJ/m²2.5--23°CkJ/m²4.024硬度测试条件测试方法测试结果单位洛氏硬度R计秤,23°C
119
R计秤,80°C
97--可燃性测试条件测试方法测试结果单位UL阻燃等级0.79mm
V-2--基本性能测试条件测试方法测试结果单位吸水率23℃，24小时ASTM D-570无水｜1.2%23℃，24小时ASTM D-5703.5%水｜-%