耐高温 PPO 基础创新塑料(美国) PPX-7110-BK1005 抗冲击 片材挤出成型
Polyphenylene Ether + PS + PP
SABIC Innovative Plastics
产品说明：
PPE+PP blend. High Impact, Good Heat Resistance
物性信息：
| 黄卡编号 | E121562-221229 |
| 特性 | 抗撞击性，高 耐热性，高 |
| 加工方法 | 片材挤出成型 注射成型 |
| 多点数据 | Coefficient of Thermal Expansion vs. Temperature (ASTM E831) Flexural DMA (ASTM D4065) Pressure-Volume-Temperature (PVT - Zoller Method) Shear DMA (ASTM D4065) Specific Heat vs. Temperature (ASTM D3417) Tensile Creep (ASTM D2990) Tensile Stress vs. Strain (ASTM D638) Viscosity vs. Shear Rate (ASTM D3835) |
| 比重 | 0.968 | g/cm³ | ASTM D792 |
| 熔流率（熔体流动速率） (260°C/5.0 kg) | 11 | g/10 min | ASTM D1238 |
| 收缩率 - 流动 (3.20 mm) | 0.80 到 1.2 | % | 内部方法 |
| 拉伸模量 1 | 1340 | MPa | ASTM D638 |
| 抗张强度 2 | ASTM D638 | ||
| 屈服 | 35.9 | MPa | ASTM D638 |
| 断裂 | 32.4 | MPa | ASTM D638 |
| 伸长率 3 | ASTM D638 | ||
| 屈服 | 6.5 | % | ASTM D638 |
| 断裂 | 200 | % | ASTM D638 |
| 弯曲模量 4(50.0 mm 跨距) | 1550 | MPa | ASTM D790 |
| 弯曲强度 5(屈服, 50.0 mm 跨距) | 51.7 | MPa | ASTM D790 |
| 悬壁梁缺口冲击强度 | ASTM D256 | ||
| -30°C | 150 | J/m | ASTM D256 |
| 23°C | 440 | J/m | ASTM D256 |
| 装有测量仪表的落镖冲击 | ASTM D3763 | ||
| -30°C, Total Energy | 27.8 | J | ASTM D3763 |
| 23°C, Total Energy | 38.0 | J | ASTM D3763 |
| 载荷下热变形温度 | ASTM D648 | ||
| 0.45 MPa, 未退火, 3.20 mm | 113 | °C | ASTM D648 |
| 1.8 MPa, 未退火, 3.20 mm | 77.2 | °C | ASTM D648 |
| 维卡软化温度 | 139 | °C | ASTM D1525 6 |
| 线形热膨胀系数 | ASTM E831 | ||
| 流动 : -40 到 40°C | 8.1E-5 | cm/cm/°C | ASTM E831 |
| 横向 : -40 到 40°C | 1.1E-4 | cm/cm/°C | ASTM E831 |
| RTI Elec | 50.0 | °C | UL 746 |
| RTI Imp | 50.0 | °C | UL 746 |
| RTI | 50.0 | °C | UL 746 |