FL 00119乙烯-醋酸乙烯共聚物#|EVA
埃克森美孚
物性信息：
| 熔流率 (190°C/2.16 kg) | 0.65 | g/10 min | ASTM D1238 |
| 醋酸乙烯含量 | 19.0 | wt% | ExxonMobil Method |
| 割线模量 (1% 正割, MD) | 54.0 | MPa | ASTM D882 |
| (1% 正割, TD) | 56.0 | MPa | ASTM D882 |
| 抗张强度 (MD: 断裂) | 33.0 | MPa | ASTM D882 |
| (TD: 断裂) | 30.0 | MPa | ASTM D882 |
| 伸长率 (MD: 断裂) | 600 | % | ASTM D882 |
| (TD: 断裂) | 650 | % | ASTM D882 |
| 维卡软化温度 | 62.0 | °C | ASTM D1525 |
埃克森美孚Escorene? Ultra EVA树脂主要型号及应用FL00012 VAC含量12%。热稳定剂。薄膜FL00014 VAC含量14%。热稳定剂。薄膜FL00112 VAC含量12%。薄膜应用FL00119 VAC含量19%。热稳定剂。薄膜FL00206 VAC含量6.5%。薄膜应用FL00208ME VAC含量8.0%。薄膜应用FL00209 VAC含量9.4%。薄膜应用FL00209CC5 VAC含量9.4%。热稳定剂,抗滑与防雾剂,特殊配方产品FL00212 VAC含量12%。热稳定剂。薄膜FL00218 VAC含量18%。热稳定剂。薄膜FL00218CH1 VAC含量114%。热稳定剂,硬脂酸锌,特殊配方产品FL00218MED VAC含量18%。热稳定剂。薄膜FL00220 VAC含量20%。热稳定剂。薄膜FL00226 VAC含量26%。薄膜级,共挤出FL00226CC VAC含量26%。热稳定剂。薄膜级,共挤出FL00909 VAC含量9.4%。薄膜应用FL00309SP VAC含量8.5%。薄膜应用FL00328 VAC含量27%。薄膜应用,共挤出FL00623 VAC含量23%。热稳定剂。薄膜级,共挤出FL00714 VAC含量14%。热稳定剂。薄膜级,共挤出FL00728 VAC含量27.5%。薄膜级,共挤出FL00728CC VAC含量27.5%。热稳定剂。薄膜级,共挤出FL00909CC1 VAC含量9.4%。防雾剂。特殊配方产品FL00909KH VAC含量9.4%。薄膜应用UL00714 VAC含量14%,注塑和挤塑及涂层UL728CC VAC含量28%,适合混合料,热熔粘合剂和薄膜UL728CC3 VAC含量28%,适合混合料,热熔粘合剂和薄膜UL00730CC3 VAC含量30%,适合薄膜等UL00909CC1 VAC含量9%,适合电缆料和注塑制品UL00909KH VAC含量9%,含有消雾剂。适合挤塑涂层制品和注塑制品UL02012 VAC含量12%,注塑级 UL02020 VAC含量20%,适合注塑和混合用料UL02133 VAC含量33%,适合混合用和热熔粘合剂UL02528 VAC含量28%,适合混合用和热熔粘合剂UL04028 VAC含量28%,适合混合用和热熔粘合剂UL04028CC VAC含量28%,适合混合用和热熔粘合剂UL04533CC VAC含量33%,适合混合用和热熔粘合剂UL05540CC VAC含量40%,适合混合用和热熔粘合剂UL08533 VAC含量33%,适合混合用和热熔粘合剂UL12530 VAC含量30%,适合混合用和热熔粘合剂UL15019 VAC含量19%,适合混合用和热熔粘合剂UL15028 VAC含量28%,适合混合用和热熔粘合剂UL40028 VAC含量28%,适合混合用和热熔粘合剂UL53019 VAC含量19%,适合混合用和热熔粘合剂UL55450 VAC含量50%,适合混合用和热熔粘合剂