拉伸强度 | ASTM D638/ISO 527 | -- | kg/cm²(MPa)[Lb/in²] | |
断裂伸长率 | ASTM D638/ISO 527 | -- | % | |
拉伸模量 | ASTM D638/ISO 527 | 2400 | kg/cm²(MPa)[Lb/in²] | |
伸长率 | ASTM D638/ISO 527 | 6.0 | % | |
弯曲模量 | ASTM D790/ISO 178 | -- | kg/cm²(MPa)[Lb/in²] | |
弯曲强度 | ASTM D790/ISO 178 | -- | kg/cm²(MPa)[Lb/in²] | |
洛氏硬度 | ASTM D785 | -- | ||
IZOD 缺口冲击强度 | 1/4" 23℃ | ASTM D256/ISO 179 | 85 | kg·cm/cm(J/M)ft·lb/in |
1/4" -30℃ | ASTM D256/ISO 179 | -- | kg·cm/cm(J/M)ft·lb/in | |
1/8" 23℃ | ASTM D256/ISO 179 | -- | kg·cm/cm(J/M)ft·lb/in | |
1/8" -30℃ | ASTM D256/ISO 179 | -- | kg·cm/cm(J/M)ft·lb/in | |
Charpy冲击强度 | 23℃ (缺口) | ASTM D256/ISO 179 | N | kg·cm/cm(J/M)ft·lb/in |
-30℃(缺口) | ASTM D256/ISO 179 | N | kg·cm/cm(J/M)ft·lb/in | |
23℃(无缺口) | ASTM D256/ISO 179 | -- | kg·cm/cm(J/M)ft·lb/in | |
-30℃(无缺口) | ASTM D256/ISO 179 | -- | kg·cm/cm(J/M)ft·lb/in | |
拉伸断裂伸长率(延伸率) | ASTM D638/ISO 527 | >50 | % |
耐候PC 德国科思创(拜耳) 2807 抗紫外线 中粘度
2023-12-13 21:20 浏览:15次