High Impact Polystyrene
Formosa Plastics Corporation
产品说明:
FCFC PS resin HP8250 meets the requirements of UL, and the certificates of environmental protection.
物性信息:
黄卡编号 | E162823-224748 |
机构评级 | EC 1907/2006 (REACH) |
RoHS 合规性 | RoHS 合规 |
UL文件号 | E162823 |
形式 | 粒子 |
加工方法 | 注射成型 |
比重 | |||
-- | 1.04 | g/cm³ | ASTM D792 |
23°C | 1.04 | g/cm³ | ISO 1183 |
熔流率(熔体流动速率) (200°C/5.0 kg) | 5.5 | g/10 min | ASTM D1238, ISO 1133 |
抗张强度 | |||
23°C | 22.6 | MPa | ASTM D638 |
23°C | 23.0 | MPa | ISO 527-2 |
伸长率 (断裂, 23°C) | 40 | % | ASTM D638, ISO 527-2 |
弯曲模量 (23°C) | 2260 | MPa | ASTM D790, ISO 178 |
弯曲强度 (23°C) | 43.0 | MPa | ASTM D790, ISO 178 |
无缺口悬臂梁冲击 (23°C, 6.35 mm) | 110 | J/m | ISO 180, ASTM D256 |
载荷下热变形温度 1(1.8 MPa, 退火, 3.18 mm) | 90.0 | °C | ASTM D648, ISO 75-2/A |
维卡软化温度 | 97.0 | °C | ASTM D1525, ISO 306/B |
UL 阻燃等级 (1.50 mm, Natural Color) | HB | UL 94 |
残余单体 | ppm |
干燥温度 | 75.0 | °C | |
干燥时间 | 1.0 到 2.0 | hr | |
料斗温度 | 40.0 | °C | |
料筒后部温度 | 190 | °C | |
料筒中部温度 | 200 | °C | |
料筒前部温度 | 210 | °C | |
射嘴温度 | 205 | °C | |
加工(熔体)温度 | 180 到 220 | °C | |
模具温度 | 20.0 到 70.0 | °C | |
注射速度 | 中等 |