LNP™ LUBRICOMP™ WFL34H compoundPolybutylene Terephthalate
SABIC Innovative Plastics
20% 玻璃纤维增强材料
产品说明:
LNP LUBRICOMP* WFL34H is a compound based on PBT resin containing 20% Glass Fiber, 15% PTFE. Added features of this material include: Wear Resistant, Healthcare.
Also known as: LNP* LUBRICOMP* Compound WFL-4034 HC
Product reorder name: WFL34H
物性信息:
填料/增强材料 | 玻璃纤维增强材料, 20% 填料按重量 |
添加剂 | PTFE润滑剂 (15%) |
特性 | 耐磨损性良好 润滑 |
用途 | 医疗/护理用品 |
加工方法 | 注射成型 |
比重 | 1.59 | g/cm³ | ASTM D792 |
收缩率 | ASTM D955 | ||
流动 : 24小时 | 0.40 到 0.70 | % | ASTM D955 |
横向流动 : 24小时 | 0.90 到 2.0 | % | ASTM D955 |
吸水率 | |||
24 hr, 50% RH | 0.050 | % | ASTM D570 |
平衡, 23°C, 50% RH | 0.070 | % | ISO 62 |
拉伸模量 | |||
-- 1 | 8750 | MPa | ASTM D638 |
-- | 8460 | MPa | ISO 527-2/1 |
抗张强度 | |||
屈服 2 | 123 | MPa | ASTM D638 |
屈服 | 121 | MPa | ISO 527-2/5 |
断裂 | 123 | MPa | ASTM D638 |
断裂 | 121 | MPa | ISO 527-2/50 |
伸长率 | |||
屈服 3 | 2.8 | % | ASTM D638 |
屈服 | 2.7 | % | ISO 527-2/50 |
断裂 | 2.8 | % | ASTM D638 |
断裂 | 2.7 | % | ISO 527-2/50 |
弯曲模量 | |||
-- | 6840 | MPa | ASTM D790 |
-- 4 | 7510 | MPa | ISO 178 |
弯曲强度 | |||
-- | 176 | MPa | ASTM D790 |
-- | 182 | MPa | ISO 178 |
屈服, 50.0 mm 跨距 5 | 177 | MPa | ASTM D790 |
摩擦系数 | ASTM D3702 Modified | ||
与自身 - 动态 | 0.48 | ASTM D3702 Modified | |
与自身 - 静态 | 0.47 | ASTM D3702 Modified | |
磨损因数 - Washer | 35.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
悬壁梁缺口冲击强度 | |||
23°C | 88 | J/m | ASTM D256 |
23°C 6 | 9.2 | kJ/m² | ISO 180/1A |
无缺口悬臂梁冲击 | |||
23°C | 820 | J/m | ASTM D4812 |
23°C 7 | 46 | kJ/m² | ISO 180/1U |
装有测量仪表的落镖冲击 | |||
23°C, Total Energy | 9.60 | J | ASTM D3763 |
-- | 3.20 | J | ISO 6603-2 |
载荷下热变形温度 | |||
0.45 MPa, 未退火, 3.20 mm | 223 | °C | ASTM D648 |
0.45 MPa, 未退火, 64.0 mm 跨距 8 | 223 | °C | ISO 75-2/Bf |
1.8 MPa, 未退火, 3.20 mm | 213 | °C | ASTM D648 |
1.8 MPa, 未退火, 64.0 mm 跨距 9 | 209 | °C | ISO 75-2/Af |
干燥温度 | 121 | °C | |
干燥时间 | 4.0 | hr | |
建议的最大水分含量 | 0.050 | % | |
料筒后部温度 | 221 到 232 | °C | |
料筒中部温度 | 243 到 254 | °C | |
料筒前部温度 | 260 到 271 | °C | |
加工(熔体)温度 | 238 到 266 | °C | |
模具温度 | 82.2 到 98.9 | °C | |
背压 | 0.172 到 0.344 | MPa | |
螺杆转速 | 30 到 60 | rpm |
1 . | 50 mm/min |
2 . | 类型 1, 5.0 mm/min |
3 . | 类型 1, 5.0 mm/min |
4 . | 2.0 mm/min |
5 . | 1.3 mm/min |
6 . | 80*10*4 |
7 . | 80*10*3 |
8 . | 80*10*4 mm |
9 . | 80*10*4 mm |