沙特沙伯基础 VALOX 732E resin PBT
VALOX™ 732E resinPolybutylene Terephthalate
SABIC Innovative Plastics
30% 玻璃矿物
产品说明：
30% glass/mineral reinforced, excellent thermal performance, low shrinkage and warp. Easy flow.
物性信息：
| 黄卡编号 | E121562-477264 |
| 填料/增强材料 | 玻璃\矿物, 30% 填料按重量 |
| 特性 | 低翘曲性 良好的流动性 收缩性低 |
| 加工方法 | 注射成型 |
| 多点数据 | Coefficient of Thermal Expansion vs. Temperature (ASTM E831) Elastic Modulus vs Temperature (ASTM D4065) Flexural DMA (ASTM D4065) Instrumented Impact (Energy) (ASTM D3763) Instrumented Impact (Load) (ASTM D3763) Pressure-Volume-Temperature (PVT - Zoller Method) Shear DMA (ASTM D4065) Specific Heat vs. Temperature (ASTM D3417) Tensile Creep (ASTM D2990) Tensile Fatigue Tensile Stress vs. Strain (ASTM D638) Thermal Conductivity vs. Temperature (ASTM E1530) Viscosity vs. Shear Rate (ASTM D3835) |
| 比重 | 1.51 | g/cm³ | ASTM D792 |
| 特定体积 | 0.663 | cm³/g | ASTM D792 |
| 收缩率 | 内部方法 | ||
| 流动 1 | 0.30 到 0.40 | % | 内部方法 |
| 流动 2 | 0.40 到 0.60 | % | 内部方法 |
| 横向流动 3 | 0.60 到 0.80 | % | 内部方法 |
| 横向流动 4 | 0.40 到 0.60 | % | 内部方法 |
| 吸水率 (24 hr) | 0.070 | % | ASTM D570 |
| 洛氏硬度 (R 级) | 109 | ASTM D785 |
| 抗张强度 5(断裂) | 82.7 | MPa | ASTM D638 |
| 伸长率 6(断裂) | 2.0 | % | ASTM D638 |
| 弯曲模量 7(50.0 mm 跨距) | 6890 | MPa | ASTM D790 |
| 弯曲强度 8(断裂, 50.0 mm 跨距) | 124 | MPa | ASTM D790 |
| 悬壁梁缺口冲击强度 (23°C) | 100 | J/m | ASTM D256 |
| 无缺口悬臂梁冲击 (23°C) | 530 | J/m | ASTM D4812 |
| 载荷下热变形温度 | ASTM D648 | ||
| 0.45 MPa, 未退火, 6.40 mm | 216 | °C | ASTM D648 |
| 1.8 MPa, 未退火, 6.40 mm | 199 | °C | ASTM D648 |
| 线形热膨胀系数 - 流动 | ASTM E831 | ||
| -40 到 40°C | 2.5E-5 | cm/cm/°C | ASTM E831 |
| 60 到 138°C | 2.5E-5 | cm/cm/°C | ASTM E831 |
| 体积电阻率 | 1.0E+17 | ohms·cm | ASTM D257 |
| 介电强度 (3.20 mm, in Oil) | 18 | kV/mm | ASTM D149 |
| 介电常数 | ASTM D150 | ||
| 50 Hz | 3.53 | ASTM D150 | |
| 60 Hz | 3.53 | ASTM D150 | |
| 1 MHz | 3.32 | ASTM D150 | |
| 耗散因数 | ASTM D150 | ||
| 50 Hz | 8.0E-3 | ASTM D150 | |
| 60 Hz | 8.0E-3 | ASTM D150 | |
| 1 MHz | 0.013 | ASTM D150 |
| 干燥温度 | 121 | °C | |
| 干燥时间 | 3.0 到 4.0 | hr | |
| 干燥时间，最大 | 12 | hr | |
| 建议的最大水分含量 | 0.020 | % | |
| 建议注射量 | 40 到 80 | % | |
| 料筒后部温度 | 243 到 254 | °C | |
| 料筒中部温度 | 249 到 260 | °C | |
| 料筒前部温度 | 254 到 266 | °C | |
| 射嘴温度 | 254 到 271 | °C | |
| 加工（熔体）温度 | 254 到 277 | °C | |
| 模具温度 | 65.6 到 93.3 | °C | |
| 背压 | 0.345 到 0.689 | MPa | |
| 螺杆转速 | 50 到 80 | rpm | |
| 排气孔深度 | 0.025 到 0.038 | mm |