PA6614G15 日本旭化成 （V2 玻纤15%, 高刚性 耐热 耐疲劳）
| 比重 (干) | 1.14 | ASTM D-792 | |
| 成型收缩率 (干) | 1.3-2.0 | % | 旭化成方法 |
| 悬臂梁式缺口冲击强度 (干(湿)) | 39(147) | J/M | ASTM D-256 |
| 拉伸强度 (干(湿)) | 79(57) | MPa | ASTM D-638 |
| 断裂延伸率 (干(湿)) | 50(250) | % | ASTM D-638 |
| 洛氏硬度 (干(湿)) | 120(108) | R scale | ASTM D-785 |
| 抗挠强度 (干(湿)) | 118(54) | MPa | ASTM D-790 |
| 抗挠系数 (干(湿)) | 2.8(1.2) | GPa | ASTM D-790 |
| 磨耗率 (湿) | 7 | ×10-6kg/1000times | ASTM D-1044 |
| 洛氏硬度 (干(湿)) | 80(55) | M scale | ASTM D-785 |
| 热变形温度 | ASTM D-648 | ||
| (0.46MPa,干) | 230 | ℃ | |
| (1.82MPa,干) | 70 | ℃ | |
| 阻燃性 (干) | V-2 | UL 94 | |
| 线性膨胀系数 (干) | 8 | ×10-5/K | ASTM D-696 |
| 导热率 (干) | 0.2 | W/(m.k) | |
| 比热容 (干) | 1670 | J/(kg.k) |