| 吸湿率 (湿) | 1.4 | % |
| 成型收缩率 (干) | 0.4/0.9 | % | 旭化成方法 |
| 比重 (干) | 1.39 | ASTM D-792 |
| 抗挠强度 (干(湿)) | 294(245) | MPa | ASTM D-790 |
| 断裂延伸率 (干(湿)) | 3(4) | % | ASTM D-638 |
| 洛氏硬度 (干(湿)) | 120(-) | R scale | ASTM D-785 |
| 拉伸强度 | 194(157) | MPa | ASTM D-638 |
| 悬臂梁式缺口冲击强度 (干(湿)) | 98(118) | J/M | ASTM D-256 |
| 洛氏硬度 (干(湿)) | 90(-) | M scale | ASTM D-785 |
| 抗挠系数 (干(湿)) | 9.6(7.6) | GPa | ASTM D-790 |
| 热变形温度 (1.82MPa,干) | 220 | ℃ | ASTM D-648 |
| 线性膨胀系数 (干) | 3 | ×10-5/K | ASTM D-696 |