RTP 300 HBPC(聚碳酸酯)安特普工程塑料(RTP Company)产品描述UL94 HB
技术参数| 密度 | 1.19 g/cm³ | ASTM D792 | |
| 熔体质量流动速率(MFR) | |||
| 300℃/1.2 kg | 10~12 g/10min | ASTM D1238 | |
| 收缩率 | |||
| - | 0.6~0.9 % | ASTM D 955 | 3.2 mm |
| 吸水率 | 0.15 % | ASTM D570 | 24 hrs, 23°C |
| 拉伸强度 | |||
| - | 59 Mpa | ASTM D 638 | |
| 拉伸延伸率 | |||
| - | 10 % | ASTM D 638 | |
| 弯曲强度 | |||
| - | 93 Mpa | ASTM D790 | |
| 弯曲模量 | 2344 Mpa | ASTM D790 | |
| 拉伸模量 | 2206 Mpa | ASTM D638 | |
| 悬臂梁缺口(Izod Notched) | |||
| - | 801 J/m | ASTM D 256 | 3.2 mm |
| 悬臂梁无缺口(Izod Unnotched) | |||
| - | NB J/m | ASTM D 4812 | 3.2 mm |
| 洛氏硬度R | 118 R | ASTM D785 | |
| 热变形温度(HDT) | |||
| 0.45 Mpa (66 psi)（4.6kg/cm²） | 138 °C | ASTM D648 | |
| 1.8 Mpa (264 psi)（18.6kg/cm²） | 132 °C | ASTM D648 | |
| UL 防火等级 | |||
| HB | 0.8 mm | UL94 | |
| 体积电阻率 | 1.0E+14 Ohm-cm | ASTM D257 | |
| 介电常数(DK) | |||
| 1MHz | 3 - | ASTM D 150 | Dry |
| 耗散因数(DF) | |||
| 1MHz | 100 E-4 | ASTM D150 | Dry |
| 绝缘强度 | 15 kV/mm | ASTM D149 | S/T, in oil |
| 耐电弧性 | 120 sec | ASTM D495 |
我司销售以下原料:
<<< PC 15/10 RBK 美国Nexus Resin ## 用途： 其它 重要参数： 熔体流动速率:10 g/10min 密度:1.21 g/cm3 缺口冲击强度:530 拉伸强度:58.6 MPa 弯曲模量:2340 MPa 热变形温度:132 ℃ 生产厂商：美国Nexus Resin集团
<<< PC 1023 美国诺瓦 ## 用途： 其它 特性备注：紫外线稳定剂 重要参数： 密度:1.2 g/cm3 缺口冲击强度:747 拉伸强度:62.1 MPa 弯曲强度:94.5 MPa 弯曲模量:2210 MPa 热变形温度:132 ℃ 生产厂商：美国诺瓦聚合物公司
<<< PC PC-115 台湾奇美 ## 用途： 其它 特性备注：低黏度 重要参数： 熔体流动速率:15 g/10min 吸水率:0.2 % 成型收缩率:0.6 % 缺口冲击强度:87 拉伸强度:61.74 MPa 弯曲强度:90.16 MPa 弯曲模量:2352 MPa 硬度:77 维卡软化点:153 ℃ 热变形温度:125 ℃ 生产厂商：台湾奇美实业股份有限公司
<<< PC 20 IR 兰蒂奇美国 ## 用途： 汽车部件 特性备注：性能特点：尺寸稳定性良好，低翘曲性，低粘度，经润滑，良好的抗蠕变性，良好的强度，高流动性，韧性良好，收缩性低，脱模性能良好，中等硬度。 重要参数： 密度:1.2 g/cm3 吸水率:0.15 % 成型收缩率:0.5 % 缺口冲击强度:800 拉伸强度:63.4 MPa 断裂伸长率:90 % 弯曲强度:100 MPa 弯曲模量:2410 MPa 硬度:118 维卡软化点:154 ℃ 热变形温度:130 ℃ 生产厂商：兰蒂奇塑料美国公司