| 添加剂 | 增滑剂 (550 ppm) |
| 熔流率（熔体流动速率） (190°C/2.16 kg) | 40 | g/10 min | ASTM D1238 |
| 肖氏硬度 | ASTM D2240 | ||
| 邵氏 A, 15 秒 | 88 | ASTM D2240 | |
| 邵氏 D, 15 秒 | 43 | ASTM D2240 |
| 抗张强度 | ASTM D638 | ||
| 屈服 | 12.3 | MPa | ASTM D638 |
| 断裂 | 7.58 | MPa | ASTM D638 |
| 伸长率 | ASTM D638 | ||
| 屈服 | 30 | % | ASTM D638 |
| 断裂 | 110 | % | ASTM D638 |
| 弯曲模量 - 1% 正割 | 279 | MPa | ASTM D790 |
| 装有测量仪表的落镖冲击 | ASTM D3763 | ||
| 0°C | 21.7 | J | ASTM D3763 |
| 23°C | 19.0 | J | ASTM D3763 |
| 维卡软化温度 | 86.0 | °C | ASTM D1525 |