原料技术数据
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
| 物理性能 | 熔体指数 | ASTM D1238 | 1 | g/10min | ||
| 机械性能 | 屈服拉伸强度 | 5mm/min | ASTM D638 | 72 | MPa | |
| 屈服伸长率 | 5mm/min | ASTM D638 | 21 | % | ||
| 断裂伸长率 | 5mm/min | ASTM D638 | 73 | % | ||
| 拉伸模量 | 5mm/min | ASTM D638 | 3000 | MPa | ||
| 弯曲模量 | ASTM D790 | 2970 | MPa | |||
| Izod冲击强度 | ASTM D256 | 96 | J/m | |||
| 电气性能 | 表面电阻率 | ASTM D257 | 6E14 | Ohm | ||
| 体积电阻率 | ASTM D257 | 8E14 | Ohm.cm | |||
| 介电强度 | ASTM D149 | 18 | KV/mm | |||
| 介电常数 | ASTM D150 | 3.7 | ||||
| 介电损耗因数 | ASTM D150 | 0.005 | ||||
| 热性能 | 热变形温度 | - | 0.45Mpa | ASTM D648 | 169 | ℃ |
| - | 1.8Mpa | ASTM D648 | 110 | ℃ | ||
| 熔点 | ASTM D3418 | 178 | ℃ | |||
| 阻燃性 | UL94 | HB | ||||