Crastin杜邦系列PBT ST820--Crastin ST820 NC010 is an unreinforced Super Tough polybutylene terephthalate resin for injection molding
Crastin® PBT ST820 NC010 >PBT-I<
阻燃等级: HB
缺口冲击: 60 kJ/m²
热变形温度: 100 °C
加工方式: 注射成型 • 挤出成型 • 涂覆
材料属性: 冲击改性
符合规定: FMVSS 302 • UL
材料特性: 非增强
PBT ST820物性信息：
| 密度 | 1.03 g/cc | 0.0372 lb/in³ | |
| 1.22 g/cc | 0.0441 lb/in³ | ISO 1183 | |
| 吸水率 | 0.31 % @Thickness 2.00 mm | 0.31 % @Thickness 0.0787 in | Sim. to ISO 62 |
| 水分吸收 | 0.120 % @Thickness 2.00 mm | 0.120 % @Thickness 0.0787 in | Sim. to ISO 62 |
| 粘度 | 219200 cP @Shear Rate 5000 1/s, Temperature 250 °C | 219200 cP @Shear Rate 5000 1/s, Temperature 482 °F | ISO 11403-1 -2 |
| 742560 cP @Shear Rate 500 1/s, Temperature 250 °C | 742560 cP @Shear Rate 500 1/s, Temperature 482 °F | ISO 11403-1 -2 | |
| 线性成型收缩率,Flow | 0.019 cm/cm | 0.019 in/in | ISO 294-4 2577 |
| 0.025 cm/cm | 0.025 in/in | annealed; ISO 294-4 | |
| 线性成型收缩率，横向 | 0.018 cm/cm | 0.018 in/in | ISO 294-4 2577 |