PA9T 日本可乐丽GP2450NH BK产品说明:
该等级符合UL94,V-0可燃性等级,不含氯和溴*。它与其它含溴阻燃剂(BFR)的V-0级阻燃剂一样,具有良好的力学性能和流动性能的平衡性。
*“无卤”的标准是溴小于900ppm,氯小于900ppm,卤素总量(溴和氯)小于1500ppm。
Genestar™ GP2450NH-2聚酰胺 9T45% 玻璃纤维增强材料Kuraray Co., Ltd.产品说明:This grade meets UL94, V-0 Flammability rating without Chlorine and Bromine*. It has good balance of mechanical properties and flow-ability as well as other V-0 grades containing Bromine Flame Retardant (BFR).
*'Halogen free' follows the standards that Br is less than 900ppm, Cl is less than 900ppm, and total of halogen amount (Br and Cl) is less than 1500ppm.
Genestar™ GP2450NH-2 物性表
填料/增强材料 | 玻璃纤维增强材料, 45% 填料按重量 |
特性 | Chlorine Free 无卤 无溴 |
用途 | 电气/电子应用领域 |
比重 | 1.53 | g/cm³ | |
收缩率 | |||
流动 : 1.00 mm | 0.040 | % | |
横向流动 : 1.00 mm | 0.50 | % | |
吸水率 1(平衡, 40°C, 95%RH) | 0.80 | % |
抗张强度 | 165 | MPa | ASTM D638 |
伸长率 (断裂) | 3.0 | % | ASTM D638 |
弯曲模量 | 13000 | MPa | ASTM D790 |
弯曲强度 | 224 | MPa | ASTM D790 |
悬壁梁缺口冲击强度 | 100 | J/m | ASTM D256 |
载荷下热变形温度 (1.8 MPa, 未退火) | 285 | °C | ASTM D648 |
玻璃转化温度 | 125 | °C | |
熔融温度 | 306 | °C |
体积电阻率 | 1.0E+16 | ohms·cm | ASTM D257 |
介电强度 | 30 | kV/mm | ASTM D149 |
相比耐漏电起痕指数(CTI) | PLC 0 | UL 746 |
UL 阻燃等级 | V-0 | UL 94 |
PA9T:系列塑胶原料
PA9T日本可乐丽 N1001A,N1002A,G1352A 低磨耗 高滑动性
PA9T日本可乐丽 N1006A,G1301A 超韧耐冲
PA9T日本可乐丽 G1250A,N1000A
PA9T日本可乐丽 G1500A,G1300A
PA9T日本可乐丽 N1006C,N1001D 押出级高粘度
PA9T日本可乐丽 GR2300,GN2330,GN2450 玻纤增强防火V0
PA9T日本可乐丽 GP2450NH 玻纤增强无卤防火V0
PA9T日本可乐丽 GT2330 防火加纤超韧耐冲
PA9T日本可乐丽 GN2332 防火加纤高流动
PA9T日本可乐丽 GW2458HF 防火加纤高流动低翘曲
PA9T日本可乐丽 G1300H,G1350,G1302 玻纤增强级
PA9T日本可乐丽 430N,K1400
供应PA9T日本可乐丽430N、BT1500H、G1250A、G1300 M42BK、G1300A、G1300A-B、G1300H-F20 BK、G1302A、G2330、G2330 BK、G2330 KG003、G2330 KG004、G2330 KV006、G2450 BK、G2450-KY008、GN2200、GN2330 NC、GN2330/BK、GN2332、GN2450、GR2300、GR2300-BK、GT2330BK、GW2458、K1400、LA121 BK、N1000A、N1006A M41、N1006C H31、T1300H、T1320A、G1350H-F02-BK、G2330-NC、GR2300-NC、GW2458HF-1BK、PAM(F)11293-L、G1302-BK、G1320A、GN2330、GN2450-1BK、GW2458 BK、GW-2458HF、N1001、N1006、TA112等等.