安全帽头盔料ABS台湾奇美PA-747 超高冲击强度ABS详细说明
ABS/PA-747/台湾奇美生产企业： 台湾奇美
①原料描述部分| 通用, 高抗冲 其它 其它 | 外观颜色||
| 安全帽头盔、摩托车挡版、鞋后跟、雪地运动用品等 | ||
| 产品特性：超高冲击强度 | ||
ABS台湾奇美PA-747物性表
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 燃烧性 | File No. E56070 UL&C-UL | 1/16"HB | ||
| 熔体流动速率 | 200℃×5kg | ASTM D-1238 | 1.1 | g/10min | |
| 熔体流动速率 | 220℃×10kg | ASTM D-1238 | 12 | g/10min | |
| 比重 | ASTM D-792 | 1.03 | 23/23℃ | ||
| 机械性能 | IZOD冲击强度 | 1/4" | ASTM D-256 | 6.6 | ft.lb/in |
| IZOD冲击强度 | 1/4" | ASTM D-256 | 36 | kg.cm/cm | |
| IZOD冲击强度 | 1/8" | ASTM D-256 | 41 | kg.cm/cm | |
| 弯曲强度 | ASTM D-790 | 620 | kg/cm2 | ||
| 弯曲弹性率 | ASTM D-790 | 2.2×104 | kg/cm2 | ||
| 弯曲弹性率 | ASTM D-790 | 3.1×105 | lb/in2 | ||
| 弯曲强度 | ASTM D-790 | 8800 | lb/in2 | ||
| 洛氏硬度 | ASTM D-785 | 108 | R | ||
| 引张强度 | ASTM D-638 | 5470 | lb/in2 | ||
| IZOD冲击强度 | 1/8" | ASTM D-256 | 7.5 | ft.lb/in | |
| 引张强度 | ASTM D-638 | 385 | kg/cm2 | ||
| 伸长率 | ASTM D-638 | 30 | % | ||
| 热性能 | 热变形温度 | ASTM D-648 | 86(187) | ℉ | |
| 维卡软化点 | ASTM D-1525 | 217 | ℉ | ||
| 维卡软化点 | ASTM D-1525 | 103 | ℃ | ||
| 热变形温度 | ASTM D-648 | 97(206) | ℃ | ||
ABS 是由丙烯腈、丁二烯和苯乙烯三种化学单体合成。但实际上往往是含丁二烯的接枝共聚物与丙烯腈-苯乙烯共聚物的混合物，其中，丙烯腈占15%~35%， 丁二烯占5%~30%， 苯乙烯占40%~60%，乳液法ABS zui常见的比例是A∶B∶S=22∶17∶61，而本体法ABS 中B 的比例往往较低，约为13%。