ULTEM PEI 2400---40% Glass fiber filled, standard flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0 and 5VA listing. WRAS certification in recognized colors.
PEI 2400物性 ：
| 比重 | 1.61 g/cc | 1.61 g/cc | ASTM D792 |
| 吸水率 | 0.13 %@Time 86400 sec | 0.13 %@Time 24.0 hour | ASTM D570 |
| 平衡吸湿 | 0.90 % | 0.90 % | ASTM D570 |
| 线性成型收缩率,Flow | 0.0010 - 0.0030 cm/cm@Thickness 3.20 mm | 0.0010 - 0.0030 in/in@Thickness 0.126 in | SABIC Method |
| 熔体流动速率 | 4.2 g/10 min@Load 6.60 kg, Temperature 337 °C | 4.2 g/10 min@Load 14.6 lb, Temperature 639 °F | ASTM D1238 |
| 洛氏硬度（M 级） | 114 | 114 | ASTM D785 |
| 抗张强度(断裂) | 179 MPa | 26000 psi | Type I, 5 mm/min; ASTM D638 |
| 伸长率 (断裂) | 2.5 % | 2.5 % | Type I, 5 mm/min; ASTM D638 |
| 拉伸模量 | 11.72 GPa | 1700 ksi | 5 mm/min; ASTM D638 |
| 弯曲强度 | 241 MPa | 35000 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
| 弯曲模量 | 11.72 GPa | 1700 ksi | 2.6 mm/min, 100 mm span; ASTM D790 |
| 悬壁梁缺口冲击强度 | 1.12 J/cm | 2.10 ft-lb/in | ASTM D256 |
| 4.80 J/cm@Thickness 3.20 mm | 8.99 ft-lb/in@Thickness 0.126 in | ASTM D256 |