| 密度 (23°C) | 1.20 | g/cm³ | ISO 1183 |
| 表观密度 1 | 0.66 | g/cm³ | ISO 60 |
| 熔流率（熔体流动速率） (300°C/1.2 kg) | 20 | g/10 min | ISO 1133 |
| 溶化体积流率（MVR） (300°C/1.2 kg) | 19.0 | cm³/10min | ISO 1133 |
| 收缩率 | |||
| 垂直流动方向 | 0.50 到 0.70 | % | ISO 2577 |
| 流动方向 | 0.50 到 0.70 | % | ISO 2577 |
| 垂直流动方向 : 2.00 mm 2 | 0.70 | % | ISO 294-4 |
| 流动方向 : 2.00 mm 3 | 0.65 | % | ISO 294-4 |
| 吸水率 | ISO 62 | ||
| 饱和, 23°C | 0.30 | % | ISO 62 |
| 平衡, 23°C, 50% RH | 0.12 | % | ISO 62 |
| 球压硬度 | 116 | MPa | ISO 2039-1 |
| 拉伸模量 (23°C) | 2400 | MPa | ISO 527-2/1 |
| 拉伸应力 | ISO 527-2/50 | ||
| 屈服, 23°C | 66.0 | MPa | ISO 527-2/50 |
| 断裂, 23°C | 65.0 | MPa | ISO 527-2/50 |
| 拉伸应变 | ISO 527-2/50 | ||
| 屈服, 23°C | 6.0 | % | ISO 527-2/50 |
| 断裂, 23°C | 120 | % | ISO 527-2/50 |
| 标称拉伸断裂应变 (23°C) | > 50 | % | ISO 527-2/50 |
| 拉伸蠕变模量 | ISO 899-1 | ||
| 1 hr | 2200 | MPa | ISO 899-1 |
| 1000 hr | 1900 | MPa | ISO 899-1 |
| 弯曲模量 4(23°C) | 2350 | MPa | ISO 178 |
| 弯曲应力 5 | ISO 178 | ||
| 3.5% 应变, 23°C | 74.0 | MPa | ISO 178 |
| 23°C | 98.0 | MPa | ISO 178 |
| Flexural Strain at Flexural Strength (23°C) 6 | 7.0 | % | ISO 178 |
| Gas Permeation | ISO 2556 | ||
| Carbon Dioxide : 23°C, 25.4 µm | 18900 | cm³/m²/bar/24 hr | ISO 2556 |
| Carbon Dioxide : 23°C, 100.0 µm | 4800 | cm³/m²/bar/24 hr | ISO 2556 |
| Nitrogen : 23°C, 25.4 µm | 630 | cm³/m²/bar/24 hr | ISO 2556 |
| Nitrogen : 23°C, 100.0 µm | 160 | cm³/m²/bar/24 hr | ISO 2556 |
| Oxygen : 23°C, 25.4 µm | 3150 | cm³/m²/bar/24 hr | ISO 2556 |
| Oxygen : 23°C, 100.0 µm | 800 | cm³/m²/bar/24 hr | ISO 2556 |
| Application of Flame from Small Burner - Method K and F (2.00 mm) | K1, F1 | DIN 53438-1, -3 | |
| Burning Rate - US-FMVSS (> 1.00 mm) | passed | ISO 3795 | |
| Flash Ignition Temperature | 480 | °C | ASTM D1929 |
| Needle Flame Test | IEC 60695-11-5 | ||
| Method F : 1.50 mm | 1.0 | min | IEC 60695-11-5 |
| Method F : 2.00 mm | 2.0 | min | IEC 60695-11-5 |
| Method F : 3.00 mm | 2.0 | min | IEC 60695-11-5 |
| Method K : 1.50 mm | 0.1 | min | IEC 60695-11-5 |
| Method K : 2.00 mm | 0.1 | min | IEC 60695-11-5 |
| Method K : 3.00 mm | 0.2 | min | IEC 60695-11-5 |
| Self Ignition Temperature | 550 | °C | ASTM D1929 |
| Electrolytical Corrosion (23°C) | A1 | IEC 60426 | |
| ISO Shortname | ISO 7391-PC,MLR,(,,)-18-9 |
| 水气透过率 (23°C, 85% RH, 100 µm) | 15 | g/m²/24 hr | ISO 15106-1 |
| 简支梁缺口冲击强度 7 | ISO 7391 | ||
| -30°C, 完全断裂 | 14 | kJ/m² | ISO 7391 |
| 23°C, 局部断裂 | 65 | kJ/m² |