| 熔体流动速率 | 0.5 | g/10min | ASTM D-1238 |
| 表面硬度 | 85 | R scale | ASTM D-785 |
| 弹性弯曲系数 | 14000 | Kg/cm | ASTM D-790 |
| 断裂伸长率 | >500 | % | ASTM D-638 |
| IZOD缺口冲击强度 (-20℃) | 8 | kg.cm/cm | ASTM D-256 |
| 断裂拉伸强度 | 330 | Kg/cm | ASTM D-638 |
| IZOD缺口冲击强度 (23℃) | >50 | kg.cm/cm | ASTM D-256 |
| 热变形温度 | 98 | ℃ | ASTM D-648 |
| 维卡软化点 | 150 | ℃ | ASTM D-1525 |
| 加速老化时间 | 360 | hr | ASTM D-3012 |
| 流动性 | 300 | mm | SK |