熔体流动速率 | 27 | g/10min | ASTM D-1238 |
密度 | 0.91 | g/cm | ASTM D-1505 |
洛氏硬度 | 80 | R标尺 | ASTM D-785 |
断裂伸长率 | 500 | % | ASTM D-638 |
屈服拉伸强度 | 250 | kg/cm | ASTM D-638 |
弹性模量 | 13000 | kg/cm | ASTM D-790 |
IZOD冲击强度 | ASTM D-256 | ||
(23℃) | 9 | kg.cm/cm | |
(0℃) | 6 | kg.cm/cm | |
(-20℃) | 5 | kg.cm/cm |
热变形温度 | 80 | ℃ |
熔体流动速率 | 27 | g/10min | ASTM D-1238 |
密度 | 0.91 | g/cm | ASTM D-1505 |
洛氏硬度 | 80 | R标尺 | ASTM D-785 |
断裂伸长率 | 500 | % | ASTM D-638 |
屈服拉伸强度 | 250 | kg/cm | ASTM D-638 |
弹性模量 | 13000 | kg/cm | ASTM D-790 |
IZOD冲击强度 | ASTM D-256 | ||
(23℃) | 9 | kg.cm/cm | |
(0℃) | 6 | kg.cm/cm | |
(-20℃) | 5 | kg.cm/cm |
热变形温度 | 80 | ℃ |