| 密度 | 885 | g/cm | ASTM D1505 |
| 表面硬度 | 87 | shore A | JIS K6253 |
| 熔融指数 | |||
| (190℃) | 1.2 | g/10min | ASTM D1238 |
| (191℃) | 2.2 | g/11min | ASTM D1239 |
| 断裂强度 | 27< | Mpa | JIS K7113 |
| 断裂伸长 | 800< | % | JIS K7114 |
| 扭曲刚性 | 9 | Mpa | ASTM D1043 |
| 熔点 | 66 | ℃ | ASTM D2117 |
| 维卡软化点 | 58 | ℃ | ASTM D1525 |
| 脆化温度 | -70> | ℃ | ASTM D748 |
| 体积电阻系数 | 10< | Ω-CM | ASTM D257 |
| 介电常数 | 2.2-2.4 | ASTM D150 | |
| 介电正接 | 5*10-4> | ASTM D150 |