产品参数
性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
基本性能 | 熔体流动速率 | ASTM D-1238 | 8.0 | g/10min | |
密度 | ASTM D-1505 | 0.90 | g/cm3 | ||
机械性能 | 成型收缩率 | HPC Method | 1.6-1.8 | % | |
冲击强度 | ASTM D-256 | 3.5 | kg·cm/cm | ||
拉伸率 | ASTM D-638 | >500 | % | ||
洛氏硬度 | ASTM D-785 | 95 | R | ||
拉伸屈服强度 | ASTM D-638 | 290 | Kg/cm2 | ||
冲击强度 | ASTM D-256 | 8.0 | kg·cm/cm | ||
弹性挠曲模量 | ASTM D-790 | 16,000 | Kg/cm2 | ||
热性能 | 热变形温度 | ASTM D-648 | 120 | ℃ | |
耐热性 | 130℃老化 | HPC Method | >3,000 | hour | |
维卡软化点 | ASTM D-1525 | 145 | ℃ |