比重 | 1.24 | g/cm³ | ASTM D792 |
熔流率 (210℃/2.16 kg) | 15 到 30 | g/10 min | ASTM D1238 |
收缩性 (Hot Air: 130℃) | < 8.0 | % | ASTM D2102 |
Modulus of Elasticity | 30.0 到 40.0 | g/denier | ASTM D2256 |
玻璃转化温度 (DSC) | 55.0 到 60.0 | ℃ | ASTM D3418 |
结晶峰温 (DSC) | 160 到 170 | ℃ | ASTM D3418 |