| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
| 基本性能 | 熔体流动速率 | 190℃/5kg | 0.9 | g/10min | ||
| 熔体流动速率 | 190℃/2.16kg | 0.2 | g/10min | |||
| 熔体流动速率 | 190℃/21.6kg | 22 | g/10min | |||
| 密度 | 923 | kg/m3 | ||||
| 物理性能 | 雾度 | ASTM D-1003 | 70 | ％ | ||
| 光泽 | ASTM D-2457 | 10 | ||||
| 机械性能 | 落锤冲击 | ISO 7765/1 | 300 | g | ||
| 击穿阻力 | force | ASTM 5748 | 65 | N | ||
| 击穿阻力 | energy | ASTM 5748 | 5 | J | ||
| 埃尔门多夫撕裂强度 | MD | ISO 6383/2 | 3 | N | ||
| TD | ISO 6383/2 | 11 | N | |||
| 断裂拉伸强度 | MD | ISO 527-3 | 450 | ％ | ||
| TD | ISO 527-3 | 750 | ％ | |||
| 拉伸模量 | MD | ASTM D-882-A | 250 | MPa | ||
| TD | ASTM D-882-A | 300 | MPa | |||
| 拉伸强度 | MD | ISO 527-3 | 55 | MPa | ||
| TD | ISO 527-3 | 45 | MPa | |||
| 其它性能 | WVTR | 38℃/90％RH | ISO 15106-2 | 8 | g/m2*d | |
| 氧气输送率 | 25℃/0％RH | ASTM D-3985 | 5000 | cm3/m2d*bar | ||