CM3006聚亚己基己二酸酰胺#聚己二酰己二胺|尼龙66|PA66
日本东丽
填充物:注塑
物性信息：
| 吸水率 (23℃) | 无水|3.5%水1.2|- | % | ASTM D-570 |
| 比重 | 无水|3.5%水1.13-1.14|- | ASTM D-792 | |
| 泰伯磨耗量 (1000g,CS-17) | 无水|3.5%水8|- | mg/1000次 | ASTM D-1044 |
| IZOD冲击强度 (23℃.无缺口1/8) | 无水|3.5%水无断裂|- | kg.cm/cm | |
| 挠曲模量 (23℃) | 无水|3.5%水29000|14000 | Kg/cm | ASTM D-790 |
| 洛氏硬度 (23℃) | 无水|3.5%水97|- | ASTM D-785 | |
| 挠曲强度 | ASTM D-790 | ||
| (80℃) | 无水|3.5%水640|400 | Kg/cm | |
| (-40℃) | 无水|3.5%水1450|1300 | Kg/cm | |
| IZOD冲击强度 (23℃.无缺口1/2) | 无水|3.5%水5|28 | kg.cm/cm | |
| 抗剪强度 (23℃) | 无水|3.5%水790|770 | Kg/cm | ASTM D-732 |
| 断裂伸长率 (23℃) | 无水|3.5%水90|< 200 | % | ASTM D-638 |
| 抗拉屈服强度 | ASTM D-638 | ||
| (23℃) | 无水|3.5%水800|530 | Kg/cm | |
| (80℃) | 无水|3.5%水430|430 | Kg/cm | |
| 挠曲强度 (23℃) | 无水|3.5%水1150|650 | Kg/cm | ASTM D-790 |
| 洛氏硬度 (23℃) | 无水|3.5%水119|100 | R | ASTM D-785 |
| 挠曲模量 (-40℃) | 无水|3.5%水44000|42000 | Kg/cm | ASTM D-790 |
| 压缩强度 (23℃) | 无水|3.5%水910|- | Kg/cm | ASTM D-695 |
| IZOD冲击强度 (-40℃.无缺口1/2) | 无水|3.5%水3.5|- | kg.cm/cm | |
| 抗拉屈服强度 (-40℃) | 无水|3.5%水1150|1100 | Kg/cm | ASTM D-638 |
| 挠曲模量 (80℃) | 无水|3.5%水9000|5000 | Kg/cm | ASTM D-790 |
| 抗拉断裂强度 (23℃) | 无水|3.5%水700|730 | Kg/cm | ASTM D-638 |
| 体积电阻率 | 无水|3.5%水 10-10|10-10 | Ω.cm | ASTM D-257 |
| 介电常数 (50HZ) | 无水|3.5%水1.6|- | ASTM D-150 | |
| 损耗因素 (50Hz) | 无水|3.5%水0.06|- | ASTM D-150 | |
| IEC导电径踪指数 | 无水|3.5%水-|530 | V | UL 746 |
| 热挠曲温度 (4.6kg/cm) | 无水|3.5%水220|- | ℃ | ASTM D-648 |
| 熔点 | 无水|3.5%水265|- | ℃ | 差示扫描测热计DSC法 |
| 线性热膨胀系数 | 无水|3.5%水9-10|- | 10-5cm/cm | ASTM D-696 |
| UL-94抗燃级 (1/16") | 无水|3.5%水|无水|3.5%水V-2|-|V-2 |- | UL 94 | |
| 导热系数 | 无水|3.5%水0.21|- | Kcal/m.hr.°C | |
| 比热 | 无水|3.5%水0.4|- | Cal/g.°C |