产品详细介绍Surlyn® 8940乙烯甲基丙烯酸DuPont Packaging & Industrial Polymers产品说明：
Surlyn® 8940 is a sodium ionomer thermoplastic resin. Itis available for use in conventional extrusion and injectione, to create various sheets or shapes.
Surlyn® 8940 thermoplastic resin is an advancedethylene/methacrylic acid (E/MAA) copolymer, in which the MAA acidgroups have been partially neutralized with sodium ions.
Surlyn® 8940 物性表
基本信息
| 特性 | 共聚物 |
| 机构评级 | FDA 21 CFR 177.1330(a) |
| 形式 | 粒子 |
物理性能额定值单位制测试方法
| 比重 | 0.950 | g/cm³ | ASTM D792, ISO 1183 |
| 熔流率（熔体流动速率） (190°C/2.16 kg) | 2.8 | g/10 min | ASTM D1238, ISO 1133 |
| 离子类型 | Sodium |
|
|
机械性能额定值单位制测试方法
| 抗磨损性 - NBS Index | 370 |
| ASTM D1630 |
热性能额定值单位制测试方法
| Freezing Point |
|
|
|
| -- | 59 | °C | ISO 3146 |
| -- | 59 | °C | ASTM D3418 |
硬度额定值单位制测试方法
| 肖氏硬度 (邵氏 D) | 65 |
| ASTM D2240, ISO 868 |
机械性能额定值单位制测试方法
| 抗张强度 (断裂, 23°C) | 33.0 | MPa | ASTM D638, ISO 527-2 |
| 伸长率 (断裂, 23°C) | 470 | % | ASTM D638, ISO 527-2 |
| 弯曲模量 |
|
| ASTM D790 |
| -20°C | 717 | MPa | ASTM D790 |
| 23°C | 350 | MPa | ASTM D790 |
| 弯曲强度 (屈服) | 15.0 | MPa | ASTM D790 |
弹性体额定值单位制测试方法
| 撕裂强度 (23°C) | 1.48 | kN/m | ASTM D624 |
冲击性能额定值单位制测试方法
| 悬壁梁缺口冲击强度 (23°C) | 1000 | J/m | ASTM D256 |
| 拉伸冲击强度 |
|
| ASTM D1822 |
| -40°C | 757 | kJ/m² | ASTM D1822 |
| 23°C | 1020 | kJ/m² | ASTM D1822 |
热性能额定值单位制测试方法
| 脆化温度 | -106 | °C | ASTM D746 |
| 维卡软化温度 | 63.0 | °C | ASTM D1525, ISO 306 |
| 熔融峰值温度 | 94.0 | °C | ASTM D3418, ISO 3146 |
光学性能额定值单位制测试方法
| 雾度 (6350 µm) | 5.0 | % | ASTM D1003 |
注射额定值单位制
| 加工（熔体）温度 | 185 到 285 | °C |
|