标准说明 :全工艺冷轧无取向电工钢带
产品形态:晶粒无取向电工钢
牌号解释
B:宝钢，BAOSTEEL
50:公称厚度(mm)的100倍
AH:无取向，高磁感型
600:铁损保证值P15/50(W/kg)的100倍
术语和定义
3.1 铁损（比总损耗） iron loss ( specific total loss)
铁损是指在交变磁场下磁化试样时，消耗在试样上的无效电能。在给定频率和大磁感应强度进行磁化的情况下，铁损用符号P(10Bm/f)表示，单位为W/kg。
表 4
| 类型 | 牌号 | 公称厚度 mm | 理论密度 kg/dm3 | 铁损P15/50 W/kg 不大于 | 磁感应强度峰值B50 T 不小于 | 叠装系数 % 不小于 | ||
| 普 通 型 | B35A210 | 0.35 | 7.60 | 2.10 | 1.62 | 95.0 | ||
| B35A230 | 7.60 | 2.30 | 1.62 | |||||
| B35A250 | 7.60 | 2.50 | 1.62 | |||||
| B35A270 | 7.65 | 2.70 | 1.62 | |||||
| B35A300 | 7.65 | 3.00 | 1.62 | |||||
| B35A360 | 7.65 | 3.60 | 1.63 | |||||
| B35A440 | 7.70 | 4.40 | 1.65 | |||||
| B35A550 | 7.75 | 5.50 | 1.66 | |||||
| B50A230 | 0.50 | 7.60 | 2.30 | 1.62 | 96.0 | |||
| B50A250 | 7.60 | 2.50 | 1.62 | |||||
| B50A270 | 7.60 | 2.70 | 1.62 | |||||
| B50A290 | 7.60 | 2.90 | 1.62 | |||||
| B50A310 | 7.65 | 3.10 | 1.62 | |||||
| B50A350 | 7.65 | 3.50 | 1.62 | |||||
| B50A400 | 7.65 | 4.00 | 1.63 | |||||
| B50A470 | 7.70 | 4.70 | 1.64 | 97.0 | ||||
| B50A540 | 7.70 | 5.40 | 1.65 | |||||
| B50A600 | 7.75 | 6.00 | 1.66 | |||||
| B50A700 | 7.80 | 7.00 | 1.70 | |||||
| B50A800 | 7.80 | 8.00 | 1.70 | |||||
| B50A1000 | 7.85 | 10.00 | 1.70 | |||||
| B50A1300 | 7.85 | 13.00 | 1.70 | |||||
| B65A600 | 0.65 | 7.75 | 6.00 | 1.64 | 97.0 | |||
| B65A700 | 7.75 | 7.00 | 1.65 | |||||
| B65A800 | 7.80 | 8.00 | 1.69 | |||||
| B65A1000 | 7.80 | 10.00 | 1.69 | |||||
| B65A1300 | 7.85 | 13.00 | 1.69 | |||||
| B65A1600 | 7.85 | 16.00 | 1.69 | |||||
| 消除应力退火型a | B35AR300 | 0.35 | 7.80 | 3.00 | 1.73 | 95.0 | ||
| B50AR300 | 0.50 | 7.75 | 3.00 | 1.72 | 96.0 | |||
| B50AR350 | 7.80 | 3.50 | 1.74 | |||||
| B50AR500 | 7.80 | 5.00 | 1.72 | |||||
| B50AR600 | 7.85 | 6.00 | 1.72 | |||||
| 高磁感型 | B35AH230 | 0.35 | 7.65 | 2.30 | 1.66 | 95.0 | ||
| B35AH250 | 7.65 | 2.50 | 1.67 | |||||
| B35AH300 | 7.70 | 3.00 | 1.69 | |||||
| B50AH300 | 0.50 | 7.65 | 3.00 | 1.67 | 96.0 | |||
| B50AH350 | 7.70 | 3.50 | 1.70 | |||||
| B50AH470 | 7.75 | 4.70 | 1.72 | |||||
| B50AH600 | 7.75 | 6.00 | 1.72 | |||||
| B50AH800 | 7.80 | 8.00 | 1.74 | |||||
| B50AH1000 | 7.75 | 10.00 | 1.75 | |||||
a 消除应力退火材的磁特性保证值仅适用于在750℃下，经2小时消除应力退火后的试样。 | ||||||||