物性信息：
| 比重 | 2.12 - 2.17 g/cc | 2.12 - 2.17 g/cc | ASTM D792 |
| 吸水率 | <= 0.050 % | <= 0.050 % | 24 hours; ASTM D570 |
| 熔体流动速率 | 1.7 - 3.0 g/10 min | 1.7 - 3.0 g/10 min | ASTM D3307 |
| 肖氏硬度 (邵氏 D) | 55 | 55 | ASTM D2240 |
| 极限抗拉强度 | 28.0 MPa | 4060 psi | ASTM D3307 |
| 15.0 MPa @Temperature 200 °C | 2180 psi @Temperature 392 °F | ASTM D3307 | |
| 抗张强度(屈服) | 14.0 MPa | 2030 psi | ASTM D3307 |
| 伸长率 (断裂) | 260 % | 260 % | ASTM D3307 |
| 450 % @Temperature 200 °C | 450 % @Temperature 392 °F | ASTM D3307 | |
| 弯曲模量 | 0.600 GPa | 87.0 ksi | ASTM D790 |
| 悬壁梁缺口冲击强度 | NB | NB | ASTM D256 |
| 体积电阻率 | 1.00e+18 ohm-cm | 1.00e+18 ohm-cm | ASTM D257 |
| 表面电阻率 | >= 1.00e+17 ohm | >= 1.00e+17 ohm | ASTM D257 |
| 介电常数 | 2.02 - 2.08 @Frequency 100 - 1.00e+7 Hz | 2.02 - 2.08 @Frequency 100 - 1.00e+7 Hz | ASTM D150 |
| 介电强度 | 80.0 kV/mm @Thickness 0.0250 mm | 2030 kV/in @Thickness 0.000984 in | film; ASTM D149 |
| 耗散因数 | <= 0.00030 @Frequency 100 - 1.00e+7 Hz | <= 0.00030 @Frequency 100 - 1.00e+7 Hz | ASTM D150 |
| 耐电弧性 | >= 180 sec | >= 180 sec | ASTM D495 |
| 线性热膨胀系数 | 150 µm/m-°C @Temperature 21.0 - 100 °C | 83.3 µin/in-°F @Temperature 69.8 - 212 °F | ASTM D696 |
| 230 µm/m-°C @Temperature 100 - 149 °C | 128 µin/in-°F @Temperature 212 - 300 °F | ASTM D696 | |
| 290 µm/m-°C @Temperature 149 - 208 °C | 161 µin/in-°F @Temperature 300 - 406 °F | ASTMD 696 | |
| 熔融温度 | 285 - 300 °C | 545 - 572 °F | ASTM D3418 |
| 可燃性(UL94) | V-0 | V-0 | |
| 极限氧指数 | >= 95 % | >= 95 % | ASTM D2863 |
| 加工温度 | 379 - 399 °C | 714 - 750 °F | Cure Temperature |
| 20% Hydrochloric Acid Transmission, g/100sq in. | <0.02 | |
| 50% Sodium Hydroxide Transmission, g/100sq in. | <.02 | |
| Acetic Acid Transmission, g/100sq in. | 0.41 | |
| Acetone Transmission, g/100sq in. | 0.95 | |
| Acetophenone Transmission, g/100sq in. | 0.5 | |
| Benzene Transmission, g/100sq in. | 0.64 | |
| Carbon Tetrachloride Transmission, g/100sq in. | 0.31 | |
| Chemical/Solvent Resistance | Excellent | |
| Ethyl Acetate Transmission, g/100sq in. | 0.76 | |
| Heat of Combustion J/g | 5300 | ASTM D240 |
| Hexane Transmission, g/100sq in. | 0.56 | |
| Piperidine Transmission, g/100sq in. | 0.04 | |
| Red Fuming Nitric Acid Transmission, g/100sq in. | 7.5-1.4 | |
| Salt Spray Resistance on aluminum, Hours | 1000 | |
| Sulfuric Acid Transmission, g/100sq in. | 0.00001 | |
| Water Transmission, g/100sq in. | 0.4 | |
| Weather Resistance | 10 | Years unaffected in Florida Exposure |