| NKT322 | ||||||||||||
| 铜合金 | ||||||||||||
| 【化学成份】Chemical composition | 【机械特性】Mechanical Properties | |||||||||||
| Cu | Ti | Fe | Temper | Tensile strength | Yield strength | Elongation | Hardness | Bendability | ||||
| balance | 3.20% | 0.20% | (N/m㎡) | (N/m㎡) | % | HV | 90° 折弯 | |||||
| 厚度≦0.5mm | ||||||||||||
| 【物理特性】Physical properties | 状态 | 抗张（拉）强度 | 屈服强度 | 延伸率 | 硬度 | G/W | B/W | |||||
| Specific Gravity | g/c㎥ | 8.7 | H | 900-1000 | 800-900 | 12.0min(18.0) | 290-350 | |||||
| 比重 | ||||||||||||
| Electrical conductivity | %IACS | 12 | EH | 920-1020 | 850-950 | 10.0min(15.0) | 300-360 | |||||
| 导电率 | ||||||||||||
| Thermal Conductivity | W/(m.k) | 54 | SH | 970-1100 | 900-1000 | 6.0min(10.0) | 310-370 | |||||
| 热传导系数 | ||||||||||||
| Specific Resistance | (nΩ.m)(@20℃) | 144 | ESH | 1010-1200 | 950-1050 | 3.0min(5.0) | 320-380 | |||||
| 电阻率 | ||||||||||||
| Modulus of Elastictity | Gpa | 120 | ||||||||||
| 弹性指数 | ||||||||||||
钛铜是无铍的超高强度铜合金，比磷青铜拥有更高的强度、为微型端子提供足够接触力的材料。拥有铍相同的强度，可以代替铍铜的使用。钛铜主要用于制作飞机发动机压气部件，为火箭、导弹和高速飞机的结构件等。钛铜在电气、电子工业中应用较多，用量大。钛铜合金具有高强度、高弹性、耐热性、抗疲劳性以及良好的折弯曲性能。