VESTAKEEP® L4000G

Polyetheretherketone

Evonik Industries AG

产品说明：

High-viscosity, unreinforced polyether ether ketone

VESTAKEEP L4000G is a high-viscosity, unreinforced lubricated polyether ether ketone for injection molding and extrusion.

The semi-crystalline polymer features superior thermal and chemical resistance. Parts made from VESTAKEEP L4000G are self extinguishing.

VESTAKEEP L4000G can be processed by common machines for thermoplastics.

The additional lubrication agent improves the feeding process.

We recommend a melt temperature between 370°C and 380°C during the injection molding process. The mold temperature should be within a range of 160°C to 200°C, preferably 180°C.

物性信息：

基本信息

黄卡编号	E100203-100947906
添加剂	润滑剂
特性	半结晶 耐化学性良好 润滑 粘度，高 自熄
形式	颗粒
加工方法	挤出 注射成型

物理性能额定值单位制测试方法

密度 (23°C)	1.30	g/cm³	ISO 1183
溶化体积流率（MVR） (380°C/5.0 kg)	12.0	cm³/10min	ISO 1133
收缩率 1			ISO 294-4
垂直流动方向 : 180°C, 2.00 mm	1.1	%	ISO 294-4
流动方向 : 180°C, 2.00 mm	0.90	%	ISO 294-4

机械性能额定值单位制测试方法

拉伸模量	3500	MPa	ISO 527-2
拉伸应力 (屈服)	96.0	MPa	ISO 527-2
拉伸应变			ISO 527-2
屈服	5.0	%	ISO 527-2
断裂	30	%	ISO 527-2

冲击性能额定值单位制测试方法

简支梁缺口冲击强度			ISO 179/1eA
-30°C, 完全断裂	6.0	kJ/m²	ISO 179/1eA
23°C, 完全断裂	7.0	kJ/m²	ISO 179/1eA
简支梁无缺口冲击强度			ISO 179/1eU
-30°C	无断裂		ISO 179/1eU
23°C	无断裂		ISO 179/1eU

热性能额定值单位制测试方法

维卡软化温度
--	335	°C	ISO 306/A
--	305	°C	ISO 306/B
熔融温度 2	340	°C	ISO 11357-3
线形热膨胀系数 - 流动 (23 到 55°C)	6.0E-5	cm/cm/°C	ISO 11359-2

电气性能额定值单位制测试方法

表面电阻率	1.0E+14	ohms	IEC 60093
体积电阻率	1.0E+15	ohms·cm	IEC 60093
介电强度 3	16	kV/mm	IEC 60243-1
相对电容率			IEC 60250
50 Hz	2.80		IEC 60250
1 MHz	2.80		IEC 60250
漏电起痕指数			IEC 60112
解决方案 A 4	175	V	IEC 60112
解决方案 A	200	V	IEC 60112

可燃性额定值单位制测试方法

UL 阻燃等级 (3.20 mm)	V-0		UL 94
灼热丝易燃指数 (2.00 mm)	960	°C	IEC 60695-2-12
热灯丝点火温度 (2.00 mm)	825	°C	IEC 60695-2-13

注射额定值单位制

加工（熔体）温度	370 到 380	°C
模具温度	160 到 200	°C

备注

1 .	determined on 2 mm sheets with film gate at rim mold temperature 180°C
2 .	2nd heating
3 .	K20/P50
4 .	100 drops value