Asahi Kasei Xyron® 300V Modified Polyphenylene EtherPolyphenylene Ether, Heat Resistant
Asahi Kasei
产品说明：
Flame Retardant
Information provided by Asahi Kasei
物性信息：
| 比重 | 1.08 g/cc | 1.08 g/cc | 23°C; ASTM D792 |
| 水分吸收 | 0.100 % | 0.100 % | 23°C, 50% RH 24 hours; ASTM D570 |
| 线性成型收缩率 | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ASTM D955 |
| 抗张强度(屈服) | 44.0 MPa | 6380 psi | 23°C, 50% RH; ASTM D638 |
| 伸长率 (断裂) | 50 % | 50 % | 23°C, 50% RH; ASTM D638 |
| 弯曲强度 | 70.0 MPa | 10200 psi | 23°C, 50% RH; ASTM D790 |
| 弯曲模量 | 2.35 GPa | 341 ksi | 23°C, 50% RH; ASTM D790 |
| 悬壁梁缺口冲击强度 | 1.76 J/cm @Thickness 6.40 mm, Temperature 23.0 °C | 3.30 ft-lb/in @Thickness 0.252 in, Temperature 73.4 °F | ASTM D256 |
| 2.30 J/cm @Thickness 3.20 mm, Temperature 23.0 °C | 4.31 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F | ASTM D256 |
| 体积电阻率 | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | 50% RH; ASTM D257 |
| 表面电阻 | 1.00e+16 ohm | 1.00e+16 ohm | 50% RH; ASTM D257 |
| 介电常数 | 2.9 @Frequency 1e+6 Hz | 2.9 @Frequency 1e+6 Hz | 50% RH; ASTM D150 |
| 2.9 @Frequency 1e+6 Hz | 2.9 @Frequency 1e+6 Hz | 50% RH; ASTM D150 | |
| 介电强度 | 25.0 kV/mm @Thickness 2.00 mm | 635 kV/in @Thickness 0.0787 in | Short time; ASTM D149 |
| 耗散因数 | 0.0030 @Frequency 60 Hz | 0.0030 @Frequency 60 Hz | 50% RH; ASTM D150 |
| 0.0040 @Frequency 1e+6 Hz | 0.0040 @Frequency 1e+6 Hz | 50% RH; ASTM D150 | |
| 耐电弧性 | 70 sec | 70 sec | Tungsten; ASTM D495 |
| 线性热膨胀系数 | 75.0 µm/m-°C @Temperature -30.0 - 60.0 °C | 41.7 µin/in-°F @Temperature -22.0 - 140 °F | ASTM D696 |
| 载荷下热变形温度(1.8 MPa) | 100 °C | 212 °F | ASTM D648 |
| 可燃性(UL94) | V-1 @Thickness 1.60 mm | V-1 @Thickness 0.0630 in | |
| V-1 @Thickness 3.20 mm | V-1 @Thickness 0.126 in |
| 加工温度 | 220 - 270 °C | 428 - 518 °F | Resin Temperature |
| 模具温度 | 50.0 - 80.0 °C | 122 - 176 °F | |
| 干燥温度 | 90.0 - 100 °C | 194 - 212 °F | Pre-drying Temperature |
| 干燥时间 | 2 - 4 hour | 2 - 4 hour |