PA66美国奥升德21SPC
2023-10-13 05:52  浏览:10
PA66美国奥升德21SPCVydyne® 21SPC

Polyamide 66

Ascend Performance Materials Operations LLC

产品说明:

Vydyne 21SPC is a general-purpose PA66 resin. Available in natural color. It is designed principally for injection-molding fabrication. This resin offers a well balanced combination of engineering properties characterized by high strength; rigidity; good toughness; high melt point; good surface lubricity; abrasion resistance; and resistance to many chemicals, machine and motor oils, solvents and gasoline.

Vydyne 21SPC permits production of molded parts with good initial color plus good property and color retention when using regrind. This resin is recognized by Underwriters Laboratories and conforms to the requirements of many industrial, federal and military specifications for premium-quality, general-purpose PA66 resins.

Internally and externally lubricated for improved machine feed and exceptional mold release. Vydyne 21SPC is intended for use in high-productivity applications. In many applications, the molding cycle can be reduced because parts may be removed from the cavity at higher temperatures. In difficult molds where parts have a tendency to stick in the cavity, Vydyne 21SPC can reduce or eliminate the need for mold release sprays. Critical molded-part dimensions should be checked against specifications before implementing shorter molding cycles on a routine production basis.

Typical Applications/End Uses:
Vydyne 21SPC has been used in many molding applications such as terminal blocks, bearings, bushings, cams, electrical connectors and housings, electrical cable ties/tie straps and many other hardware and general industrial parts.

物性信息:

基本信息
黄卡编号

E70062-249058

添加剂

润滑剂

特性

刚性,高

高强度

抗溶剂性

快的成型周期

良好耐磨损性

耐化学性良好

耐汽油性

耐油性能

韧性良好

润滑

通用

脱模性能良好

用途

衬套

工业应用

连接器

凸轮

外壳

轴承

机构评级

ASTM D 4066 PA0111

ASTM D 6779 PA0111

FDA 21 CFR 177.1500

FED L-P-410A

MIL M-20693B

RoHS 合规性

RoHS 合规

UL文件号

E70062

外观

自然色

形式

粒子

加工方法

注射成型

多点数据

Isothermal Stress vs. Strain (ISO 11403-1)

物理性能干燥调节后的单位制测试方法密度1.14--g/cm³ISO 1183收缩率


ISO 294-4     垂直流动方向 : 23°C, 2.00 mm1.7--%ISO 294-4     流动方向 : 23°C, 2.00 mm1.8--%ISO 294-4吸水率


ISO 62     23°C, 24 hr1.2--%ISO 62     平衡, 23°C, 50% RH2.4--%ISO 62室外适用性f2--
UL 746C机械性能干燥调节后的单位制测试方法拉伸模量 (23°C)31001400MPaISO 527-2拉伸应力


ISO 527-2     屈服, 23°C82.055.0MPaISO 527-2     断裂, 23°C55.045.0MPaISO 527-2拉伸应变 (屈服, 23°C)5.025%ISO 527-2标称拉伸断裂应变 (23°C)25> 50%ISO 527-2弯曲模量 (23°C)29001500MPaISO 178弯曲强度 (23°C)80.050.0MPaISO 178泊松比0.40--
ISO 527冲击性能干燥调节后的单位制测试方法简支梁缺口冲击强度


ISO 179/1eA     -30°C5.07.0kJ/m²ISO 179/1eA     23°C6.020kJ/m²ISO 179/1eA简支梁无缺口冲击强度


ISO 179/1eU     -30°C无断裂无断裂
ISO 179/1eU     23°C无断裂无断裂
ISO 179/1eU悬壁梁缺口冲击强度


ISO 180     -30°C5.07.0kJ/m²ISO 180     23°C6.020kJ/m²ISO 180热性能干燥调节后的单位制测试方法热变形温度



     0.45 MPa, 未退火200--°CISO 75-2/B     1.8 MPa, 未退火70.0--°CISO 75-2/A熔融温度260--°CISO 11357-3线形热膨胀系数


ISO 11359-2     流动 : 23 到 55°C1.0E-4--cm/cm/°CISO 11359-2     横向 : 23 到 55°C1.0E-4--cm/cm/°CISO 11359-2RTI Elec


UL 746     0.400 mm130--°CUL 746     0.710 mm130--°CUL 746     1.50 mm130--°CUL 746     3.00 mm130--°CUL 746RTI Imp


UL 746     0.400 mm75.0--°CUL 746     0.710 mm75.0--°CUL 746     1.50 mm75.0--°CUL 746     3.00 mm75.0--°CUL 746RTI


UL 746     0.400 mm75.0--°CUL 746     0.710 mm85.0--°CUL 746     1.50 mm85.0--°CUL 746     3.00 mm85.0--°CUL 746电气性能干燥调节后的单位制测试方法体积电阻率 (0.750 mm)1.0E+13--ohms·cmIEC 60093介电强度 (1.00 mm)26--kV/mmIEC 60243耐电弧性 (3.00 mm)PLC 5--
ASTM D495漏电起痕指数 (3.00 mm)600--VIEC 60112高电弧燃烧指数(HAI)


UL 746     0.400 mmPLC 1--
UL 746     0.710 mmPLC 0--
UL 746     1.50 mmPLC 0--
UL 746     3.00 mmPLC 0--
UL 746高电压电弧起痕速率 (HVTR)PLC 0--
UL 746热丝引燃 (HWI)


UL 746     0.400 mmPLC 4--
UL 746     0.710 mmPLC 4--
UL 746     1.50 mmPLC 3--
UL 746     3.00 mmPLC 2--
UL 746可燃性干燥调节后的单位制测试方法UL 阻燃等级


UL 94     0.400 mmV-2--
UL 94     0.710 mmV-2--
UL 94     1.50 mmV-2--
UL 94     3.00 mmV-2--
UL 94灼热丝易燃指数


IEC 60695-2-12     0.400 mm960--°CIEC 60695-2-12     0.710 mm960--°CIEC 60695-2-12     1.50 mm960--°CIEC 60695-2-12     3.00 mm960--°CIEC 60695-2-12热灯丝点火温度


IEC 60695-2-13     0.400 mm825--°CIEC 60695-2-13     0.710 mm850--°CIEC 60695-2-13     1.50 mm850--°CIEC 60695-2-13     3.00 mm850--°CIEC 60695-2-13极限氧指数25--%ISO 4589-2注射干燥单位制
干燥温度< 70.0°C
干燥时间1.0 到 3.0hr
建议的最大回制料比例50%
料筒后部温度260 到 280°C
料筒中部温度270 到 285°C
料筒前部温度280 到 290°C
射嘴温度280 到 300°C
加工(熔体)温度285 到 300°C
模具温度65.0 到 95.0°C