尼龙6未强化 PA6 CM1041 东丽日本
2023-10-14 05:42 浏览:15次
| 性能项目 | 试验条件 | 测试方法 | 测试数据 |
| 吸水率 | 23℃，24小时 | ASTM D-570 | 无水｜1.8 | % |
| 吸水率 | 23℃，24小时 | ASTM D-570 | 3.5%水｜- | % |
| 比重 | ASTM D-792 | 无水｜1.12-1.14 |
|
|
| 比重 | ASTM D-792 | 3.5%水｜- |
|
|
| 泰伯磨耗量 | 1000g,CS-17 | ASTM D-1044 | 无水｜≤3-4 | mg/1000次 |
| 泰伯磨耗量 | 1000g,CS-17 | ASTM D-1044 | 3.5%水｜- | mg/1000次 |
| 压缩强度 | 23℃ | ASTM D-695 | 无水｜800 | Kg/cm2 |
| 压缩强度 | 23℃ | ASTM D-695 | 3.5%水｜- | Kg/cm2 |
| 洛氏硬度 | 23℃ | ASTM D-785 | 无水｜119 | R-标度 |
| 洛氏硬度 | 23℃ | ASTM D-785 | 3.5%水｜88 | R-标度 |
| 挠曲模量 | 23℃ | ASTM D-790 | 无水｜25500 | Kg/cm2 |
| 挠曲模量 | 23℃ | ASTM D-790 | 3.5%水｜8000 | Kg/cm2 |
| 抗剪强度 | 23℃ | ASTM D-732 | 无水｜720 | Kg/cm2 |
| 抗剪强度 | 23℃ | ASTM D-732 | 3.5%水｜650 | Kg/cm2 |
| IZOD冲击强度 | 23℃，无缺口1/8 | 无水｜无断裂 | kgcm/cm |
|
| IZOD冲击强度 | 23℃，无缺口1/8 | 3.5%水｜- | kgcm/cm |
|
| 挠曲模量 | -40℃ | ASTM D-790 | 无水｜39000 | Kg/cm2 |
| 挠曲模量 | -40℃ | ASTM D-790 | 3.5%水｜37000 | Kg/cm2 |
| 挠曲强度 | 80℃ | ASTM D-790 | 无水｜430 | Kg/cm2 |
| 挠曲强度 | 80℃ | ASTM D-790 | 3.5%水｜250 | Kg/cm2 |
| 抗拉屈服强度 | 80℃ | ASTM D-638 | 无水｜270 | Kg/cm2 |
| 抗拉屈服强度 | 80℃ | ASTM D-638 | 3.5%水｜200 | Kg/cm2 |
| 抗拉断裂强度 | 23℃ | ASTM D-638 | 无水｜800 | Kg/cm2 |
| 抗拉断裂强度 | 23℃ | ASTM D-638 | 3.5%水｜- | Kg/cm2 |
| 挠曲强度 | 23℃ | ASTM D-790 | 无水｜1000 | Kg/cm2 |
| 挠曲强度 | 23℃ | ASTM D-790 | 3.5%水｜400 | Kg/cm2 |
| 抗拉屈服强度 | 23℃ | ASTM D-638 | 无水｜760 | Kg/cm2 |
| 抗拉屈服强度 | 23℃ | ASTM D-638 | 3.5%水｜350 | Kg/cm2 |
| 抗拉屈服强度 | -40℃ | ASTM D-638 | 无水｜1130 | Kg/cm2 |
| 抗拉屈服强度 | -40℃ | ASTM D-638 | 3.5%水｜1000 | Kg/cm2 |
| 断裂伸长率 | 23℃ | ASTM D-638 | 无水｜<200 | % |
| 断裂伸长率 | 23℃ | ASTM D-638 | 3.5%水｜<200 | % |
| 挠曲模量 | 80℃ | ASTM D-790 | 无水｜7000 | Kg/cm2 |
| 挠曲模量 | 80℃ | ASTM D-790 | 3.5%水｜3000 | Kg/cm2 |
| 挠曲强度 | -40℃ | ASTM D-790 | 无水｜1400 | Kg/cm2 |
| 挠曲强度 | -40℃ | ASTM D-790 | 3.5%水｜1300 | Kg/cm2 |
| 损耗因素 | 50Hz | ASTM D-150 | 无水｜0.07 |
|
| 损耗因素 | 50Hz | ASTM D-150 | 3.5%水｜- |
|
| 介电常数 | 50Hz | ASTM D-150 | 无水｜4.1 |
|
| 介电常数 | 50Hz | ASTM D-150 | 3.5%水｜- |
|
| 损耗因素 | 106Hz | ASTM D-150 | 无水｜0.03 |
|
| 损耗因素 | 106Hz | ASTM D-150 | 3.5%水｜- |
|
| 介电强度 | 1/8 | ASTM D-149 | 无水｜20 | KV/mm |
| 介电强度 | 1/8 | ASTM D-149 | 3.5%水｜- | KV/mm |
| 介电常数 | 103Hz | ASTM D-150 | 无水｜3.9 |
|
| 介电常数 | 103Hz | ASTM D-150 | 3.5%水｜- |
|
| 体积电阻率 | ASTM D-257 | 无水｜1014-1015 | Ω.cm |
|
| 体积电阻率 | ASTM D-257 | 3.5%水｜1011-1012 | Ω.cm |
|
| 损耗因素 | 103Hz | ASTM D-150 | 无水｜0.06 |
|
| 损耗因素 | 103Hz | ASTM D-150 | 3.5%水｜- |
|
| 介电常数 | 106Hz | ASTM D-150 | 无水｜3.4 |
|
| 介电常数 | 106Hz | ASTM D-150 | 3.5%水｜- |
|
| 熔点 | 差示扫描测热计DSC法 | 无水｜225 | ℃ |
|
| 熔点 | 差示扫描测热计DSC法 | 3.5%水｜- | ℃ |
|
| 线性热膨胀系数 | ASTM D-696 | 无水｜8 | 10-5cm/cm |
|
| 线性热膨胀系数 | ASTM D-696 | 3.5%水｜- | 10-5cm/cm |
|
| 比热 | 无水｜0.46 | Cal/g.°C |
|
|
| 比热 | 3.5%水｜- | Cal/g.°C |
|
|
| 热挠曲温度 | 4.6kg/cm2 | ASTM D-648 |
|
|