产品说明：

ATOFINA Polypropylene PPH 10012 is a nucleated and antistatic homopolymer polypropylene obtained by controlled rheology.

Application

PPH 10012 is intended for high speed injection molding of household articles, lightweight dairy tubs and goblets and ice cream boxes.

Information provided provided by Total Petrochemicals.

Total Petrochemicals acquired former Fina and Atofina plastics product lines.

物性信息：

物理性能额定值 (公制)额定值 (英制)测试方法

体积密度	0.525 g/cc	0.0190 lb/in³	ISO 1183
密度	0.905 g/cc	0.0327 lb/in³	ISO 1183
熔体流动速率	42 g/10 min @Load 2.16 kg, Temperature 230 °C	42 g/10 min @Load 4.76 lb, Temperature 446 °F	ISO 1133

机械性能额定值 (公制)额定值 (英制)测试方法

洛氏硬度（R 级）	98	98	ISO 2039-2
抗张强度(屈服)	34.0 MPa	4930 psi	ISO 527-2
屈服伸长率	9.0 %	9.0 %	ISO 527-2
拉伸模量	1.60 GPa	232 ksi	ISO 527-2
弯曲模量	1.50 GPa	218 ksi	ISO 527-2
悬壁梁缺口冲击强度	3.00 kJ/m²	1.43 ft-lb/in²	ISO 179
简支梁缺口冲击强度	0.400 J/cm²	1.90 ft-lb/in²	ISO 179

热性能额定值 (公制)额定值 (英制)测试方法

熔融温度	165 °C	329 °F	ISO 3146
载荷下热变形温度(0.46 MPa)	105 °C	221 °F	120°C per hour; ISO 75-2
载荷下热变形温度(1.8 MPa)	58.0 °C	136 °F	120°C per hour; ISO 75-2
维卡软化温度	87.0 °C	189 °F	50N-50°C per hour; ISO 306
	152 °C	306 °F	10N-50°C per hour; ISO 306