Bormed™ RJ880MO

Polypropylene Random Copolymer

Borealis AG

产品说明：

Bormed RJ880MO is a resin intended for evaluation for use in Healthcare applications.

Bormed RJ880MO is a specially modified highly-transparent polypropylene random copolymer with very high melt flow rate. It is designed for high-speed injection moulding and contains nucleating agent and demoulding additives. Additivation has been optimized to provide good antistatic and demoulding properties without blooming or plate-out problems. This polymer is a CR (controlled rheology) grade with narrow molecular weight distribution giving low warpage. Products originating from this grade have excellent transparency, good organoleptic properties, good balance of stiffness and impact strength at ambient temperatures.

物性信息：

基本信息

添加剂 成核剂

脱模

 特性 不起霜

成核的

低翘曲性

刚性，良好

抗静电性

抗撞击性，良好

可回收材料

可控流变

良好的感官特征

流动性高

清晰度，高

脱模性能良好

无规共聚物

窄分子量分布

 用途 包装

盖子

容器

外壳

药品包装

医疗/护理用品

医用包装

 加工方法 注射成型

 物理性能额定值单位制测试方法

密度 0.905 g/cm³ ISO 1183 

熔流率（熔体流动速率） (230°C/2.16 kg) 45 g/10 min ISO 1133 

收缩率 1.0 到 2.0 %  

硬度额定值单位制测试方法

洛氏硬度 (R 计秤) 80  ISO 2039-2 

机械性能额定值单位制测试方法

拉伸模量 (1.00 mm) 1050 MPa ISO 527-2 

拉伸应力 (屈服) 27.0 MPa ISO 527-2/50 

拉伸应变 (屈服) 13 % ISO 527-2/50 

冲击性能额定值单位制测试方法

简支梁缺口冲击强度 (23°C) 5.0 kJ/m² ISO 179/1eA 

热性能额定值单位制测试方法

热变形温度 (0.45 MPa, 未退火) 73.0 °C ISO 75-2/B 

注射额定值单位制

加工（熔体）温度 210 到 260 °C  

模具温度 15.0 到 40.0 °C  

注射速度 快速   

保压 20.0 到 50.0 MPa