无卤阻燃PC 9425增强20%,高粘度

规格参数：

销售方式 :	品牌经销	牌号 :	9425
厂家(产地) :	德国	用途级别 :	电子电器部件
特性级别 :	阻燃级	加工级别 :	注塑级

[Datasheet Makrolon 9425]数据
MVR (300 °C/1.2 kg) 5.0 cm3/10 min; 20 % glass fiber reinforced; chlorine- and bromine-free flame retardancy; UL 94V-0/1.5 mm and 5VA/3.0 mm; high viscosity; easy release

☆These property characteristics are taken from the CAMPUS plastics data bank and are based on the international catalogue of basic data for plastics according to ISO 10350.
Impact properties: N = non-break, P = partial break, C = complete break

ISO Shortname:ISO 7391-PC,MFR,(,,)-05-3,GF20
Property		Test Condition	Unit	Standard	Value
Rheological properties
☆	Melt volume-flow rate	300℃;1.2 kg	cm3/10 min	ISO 1133	5
☆	Molding shrinkage,parallel	60x60x2 mm;500 bar	%	ISO 294-4	0.35
☆	Molding shrinkage,normal	60x60x2 mm;500 bar	%	ISO 294-4	0.45
.	Molding shrinkage,parallel/normal	值的范围一般实践经验的基础上	%	b.o.ISO 2577	0.3 - 0.5
.	Melt mass-flow rate	300℃;1.2 kg	g/10 min	ISO 1133	6
Mechanical properties(23℃/50 % r.h.)
☆	Tensile modulus	1 mm/min	MPa	ISO 527-1,-2	5800
☆	Stress at break	5 mm/min	MPa	ISO 527-1,-2	86
☆	Strain at break	5 mm/min	%	ISO 527-1,-2	2.6
☆	Tensile creep modulus	1 h	MPa	ISO 899-1	5700
☆	Tensile creep modulus	1000 h	MPa	ISO 899-1	5200
.	Flexural modulus	2 mm/min	MPa	ISO 178	5500
.	Flexural strength	2 mm/min	MPa	ISO 178	135
.	Flexural strain at flexural strength	2 mm/min	%	ISO 178	3.5
☆	Charpy impact strength	23℃	kJ/m2	ISO 179-1eU	40C
☆	Charpy impact strength	-30℃	kJ/m2	ISO 179-1eU	50C
.	Charpy impact strength	-60℃	kJ/m2	ISO 179-1eU	50C
.	Charpy notched impact strength	23℃;3 mm	kJ/m2	ISO 7391/b.o.ISO 179-1eA	8C
.	Izod notched impact strength	23℃;3.2 mm	kJ/m2	b.o.ISO 180-A	8C
☆	Puncture maximum force	23℃	N	ISO 6603-2	900
☆	Puncture maximum force	-30℃	N	ISO 6603-2	900
☆	Puncture energy	23℃	J	ISO 6603-2	5
☆	Puncture energy	-30℃	J	ISO 6603-2	5
.	Ball indentation hardness	.	N/mm2	ISO 2039-1	148
Thermal properties
☆	Temperature of deflection under load	1.80 MPa	℃	ISO 75-1,-2	138
☆	Temperature of deflection under load	0.45 MPa	℃	ISO 75-1,-2	142
☆	Vicat softening temperature	50 N;50℃/h	℃	ISO 306	146
.	Vicat softening temperature	50 N;120℃/h	℃	ISO 306	148
☆	线性热膨胀系数,并行	23 to 55℃	10-4/K	ISO 11359-1,-2	0.3
☆	横向线性热膨胀系数	23 to 55℃	10-4/K	ISO 11359-1,-2	0.65
☆	燃烧性能UL94(1.5毫米)[UL认可]	1.5 mm	Class	UL 94	V-0
.	燃烧性UL94 [UL认可]	0.5 mm	Class	UL 94	V-2
☆	燃烧性能UL94-5V[UL认可]	3.0 mm	Class	UL 94	5VA
☆	Oxygen index	Method A	%	ISO 4589-2	35
.	Thermal conductivity	23℃	W/(m·K)	ISO 8302	0.23
.	耐热(球压试验)	.	℃	IEC 60695-10-2	136
.	相对温度指数(拉伸强度)[UL认可]	1.5 mm	℃	UL 746B	125
.	相对温度指数(拉伸冲击强度)[UL认可]	1.5 mm	℃	UL 746B	125
.	相对温度指数(介电强度)[UL认可]	1.5 mm	℃	UL 746B	130
.	Glow wire test(GWFI)	0.75 mm	℃	IEC 60695-2-12	960
.	Glow wire test(GWFI)	1.5 mm	℃	IEC 60695-2-12	960
.	Glow wire test(GWFI)	3.0 mm	℃	IEC 60695-2-12	960
.	Glow wire test(GWIT)	0.75 mm	℃	IEC 60695-2-13	875
.	Glow wire test(GWIT)	1.5 mm	℃	IEC 60695-2-13	875
.	Glow wire test(GWIT)	3.0 mm	℃	IEC 60695-2-13	875
.	来自小燃烧器的火焰中的应用	Method K and F;2.0 mm	Class	DIN 53438-1,-3	K1,F1
.	来自小燃烧器的火焰中的应用	2 mm	Class	DIN 4102	B2
.	Needle flame test	Method K;1.5 mm	s	IEC 60695-11-5	60
.	Needle flame test	Method K;2.0 mm	s	IEC 60695-11-5	120
.	Needle flame test	Method K;3.0 mm	s	IEC 60695-11-5	120
.	Needle flame test	Method F;1.5 mm	s	IEC 60695-11-5	120
.	Needle flame test	Method F;2.0 mm	s	IEC 60695-11-5	120
.	Needle flame test	Method F;3.0 mm	s	IEC 60695-11-5	120
.	Burning rate(US-FMVSS)	>=1.0 mm	mm/min	ISO 3795	passed
.	Flash ignition temperature	.	℃	ASTM D1929	470
.	Self ignition temperature	.	℃	ASTM D1929	550
Electrical properties(23℃/50 % r.h.)
☆	Relative permittivity	100 Hz	-	IEC 60250	3.3
☆	Relative permittivity	1 MHz	-	IEC 60250	3.3
☆	Dissipation factor	100 Hz	10月4日	IEC 60250	10
☆	Dissipation factor	1 MHz	10月4日	IEC 60250	90
☆	Volume resistivity	.	Ohm·m	IEC 60093	1.00E+14
☆	< 人气 130 发布时间 2017-10-16 09:30 所属行业 PC 编号 21681150 我公司的其他供应信息 PC 9417增强10%,阻燃,高粘度,抗UV,易释放拜耳PC 9415玻纤10,氯和溴阻燃导热PP MT00E 专有填料导热材料散热性能好热传导尼龙PA6 PX11422 导电导热尼龙塑料高导热尼龙PA6 PX08322 LED导热外壳料高温尼龙PA9T 日本可乐丽 BT1500H 日本可乐丽PA9T G1300 M42BK高耐热黑色增强尼本色PA9T G1300A 可乐丽高耐热性聚酰胺树脂日本可乐丽PA9T G1300H 耐高温可过290度锡测试易焊接PA9T日本可乐丽G1300H-F02 BK高刚性尼龙相关无卤阻燃产品青岛市无卤阻燃易流动PC/ABS德国拜耳FR2000性能价格 2024-11-18 1140L4 无卤阻燃V0 40%玻纤增强PPS 2024-12-23 SEBS(无卤阻燃料)日本可乐丽4044 2024-03-13 防火加纤10 PBT德国巴斯夫B4406 G2增强10%无卤阻燃热稳定抗UV 2024-03-06 长期供应防火V0 PC广州LG GN1006FM电子电器无卤阻燃注塑级电子部件原料塑胶原料 2024-06-23 新能源充电桩线缆tpu材料耐水解无卤阻燃TPU 2024-08-17 美国杜邦PBT FR684NH1 25%玻纤增强无卤阻燃V0 通用注射成型 2024-08-18 无卤阻燃PC韩国LG化学1301V-10中等粘性Lupoy 2024-10-02 标准料 TPE 美国杜邦无卤阻燃塑料制品 6356-BKB09 汽车部件 2024-10-07 耐高温美国杜邦PA66 HTN52G30L BK337 无卤阻燃增强级汽车领域建材行业 2024-11-01 现货PBT 美国杜邦 T841FR 加玻纤10% 无卤阻燃高抗冲注塑级型材 2024-11-18 ABS 韩国LG EF-378 无卤阻燃级ABS塑料耐热性好 2024-12-20 拨打电话请卖家联系我 007商务站频道联系007商务站