POM 日本宝理 M90-44 注塑级
| 规格级别： | 注塑级 | 外观颜色： | --- |
| 用途概述： | --- | ||
| 备注说明： | 特性：共聚甲醛，高流动性及短周期。 | ||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 吸水率 | 23℃，24hr | ASTM D-570 | 0.22 | % |
| 物理性能 | 动摩擦系数对钢对夺钢 | --- | ASTM D-1894ASTM D-1894 | 0.150.35 | --- |
| 比重 | --- | ASTM D-792 | 1.41 | --- | |
| 机械性能 | 抗拉强度 | --- | ASTM D-638 | 60 | MPa |
| 拉伸率 | --- | ASTM D-638 | 60 | % | |
| 弯曲强度 | --- | ASTM D-790 | 96 | MPa | |
| 弯曲模量 | --- | ASTM D-790 | 2580 | MPa | |
| IZOD冲击强度（带缺口）缺口侧缺口背侧 | --- | ASTM D-256ASTM D-256 | 63760 | J/mJ/m | |
| 洛氏硬度 | --- | ASTM D-785 | 80 | M | |
| 电气性能 | 体积电阻系数 | --- | ASTM D-257 | 1×1014 | Ω.cm |
| 表面电阻系数 | --- | ASTM D-257 | 1×1016 | Ω | |
| 介电击穿强度 | --- | ASTM D-149 | 24 | MV/m | |
| 热 性 能 | 负荷挠曲温度 | 1.32MPa | ASTM D-648 | 110 | ℃ |
| 线膨胀系数 | --- | ASTM D-596 | 10 | ×10-5/℃ | |
| 燃烧性 | --- | UL 94 | 94HB | --- | |