原料技术数据
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 熔体流动速率 | 220℃/10kg | ASTM D-1238 | 15 | g/10min |
| 成型收缩率 | ASTM D-955 | 0.003-0.005 | mm/mm | ||
| 比重 | ASTM D-792 | 1.04 | |||
| 机械性能 | 拉伸强度 | ASTM D-638 | 480 | kg/cm2 | |
| 弯曲弹性率 | ASTM D-790 | 750 | kg/cm2 | ||
| 挠曲模量 | ASTM D-790 | 23000 | kg/cm2 | ||
| 冲击弹度 | Notched1/4" | ASTM D-256 | 30 | kgcm/cm | |
| 洛氏硬度 | R-Scale | ASTM D-785 | 101 | ||
| 延伸率 | ASTM D-638 | 25 | % | ||
| 电气性能 | HWI | UL-746A | 3 | PLCCode | |
| HAI | UL-746A | 0 | PLCCode | ||
| CTI | UL-746A | 0 | PLCCode | ||
| HVTR | UL-746A | 2 | PLCCode | ||
| 耐电弧性 | ASTM D-495 | 6 | PLCCode | ||
| 热性能 | 燃烧率 | 1/8" | UL-94 | HB | |
| 维卡软化点 | 1.000g | ASTM D-1525 | 98 | ℃ | |
| 热变形温度 | Unannealed18.5kg/cm2,1/2" | ASTM D-648 | 89 | ℃ | |
| 燃烧率 | 1/8" | IEC-707 | FH3-34 | mm/min | |
| 燃烧率 | 1/16" | UL-94 | HB | ||