Iupital是一种共聚甲醛树脂，用最新的技术及制造工艺，独自开发生产。 被广泛地用于各种工业生产,是精密器械、汽车部件、办公自动化设备以及电子设备的理想原材料。
特点：
机械性能均匀、高耐疲劳性
耐蠕变性佳
耐摩擦和耐磨损性能佳
工作温度范围广
耐油、耐药性能高
成型加工性佳
A10-03 2.20 (190°C/2.16 kg) 8.0 (23°C) 67.0 (屈服, ISO 527-1, -2) 35 (50 mm/min) 1.00E+16
A25-03 12 (190°C/2.16 kg) 8.0 (23°C) 69.0 (屈服, ISO 527-1, -2) 35 (50 mm/min) 1.00E+16
F10-01 2.20 (190°C/2.16 kg) 8.0 (23°C) 63.0 (屈服, ISO 527-1, -2) 33 (50 mm/min) 1.00E+16
F10-02 2.20 (190°C/2.16 kg) 8.0 (23°C) 63.0 (屈服, ISO 527-1, -2) 33 (50 mm/min) 1.00E+16
F10-EW 3.40 (190°C/2.16 kg) 8.0 (23°C) 62.0 (屈服, ISO 527-1, -2) 35 (50 mm/min)
F20-03 7.70 (190°C/2.16 kg) 7.0 (23°C) 64.0 (屈服, ISO 527-1, -2) 30 (50 mm/min) 1.00E+16
F20-54 7.70 (190°C/2.16 kg) 6.5 (23°C) 62.0 (屈服, ISO 527-1, -2) 30 (50 mm/min) 1.00E+16
F20-61 7.70 (190°C/2.16 kg) 6.0 (23°C) 63.0 (屈服, ISO 527-1, -2) 30 (50 mm/min) 1.00E+13
F20-EW 7.70 (190°C/2.16 kg) 7.0 (23°C) 64.0 (屈服, ISO 527-1, -2) 30 (50 mm/min)
F25-03 14 (190°C/2.16 kg) 6.5 (23°C) 64.0 (屈服, ISO 527-1, -2) 27 (50 mm/min) 1.00E+16
F30-03 23 (190°C/2.16 kg) 6.0 (23°C) 64.0 (屈服, ISO 527-1, -2) 25 (50 mm/min) 1.00E+16
F40-03 45 (190°C/2.16 kg) 5.0 (23°C) 64.0 (屈服, ISO 527-1, -2) 20 (50 mm/min) 1.00E+16
FRC-20 8.30 (190°C/2.16 kg) 8.0 (23°C) 57.0 (屈服, ISO 527-1, -2) 42 (50 mm/min)
FV-30 27 (190°C/2.16 kg) 6.0 (23°C) 63.0 (屈服, ISO 527-1, -2) 30 (50 mm/min) 1.00E+13
FL2010 6.10 (190°C/2.16 kg) 5.0 (23°C) 52.0 (屈服, ISO 527-1, -2) 18 (50 mm/min) 1.00E+16
FL2020 4.70 (190°C/2.16 kg) 5.0 (23°C) 44.0 (屈服, ISO 527-1, -2) 15 (50 mm/min) 1.00E+16
FS2022 8.60 (190°C/2.16 kg) 7.5 (23°C) 56.0 (屈服, ISO 527-1, -2) 51 (50 mm/min) 1.00E+16
FW-21 8.20 (190°C/2.16 kg) 6.5 (23°C) 56.0 (屈服, ISO 527-1, -2) 30 (50 mm/min)
FW-24 8.20 (190°C/2.16 kg) 7.0 (23°C) 51.0 (屈服, ISO 527-1, -2) 35 (50 mm/min)
FX-11 8.60 (190°C/2.16 kg) 7.0 (23°C) 55.0 (屈服, ISO 527-1, -2) 35 (50 mm/min) 1.00E+16
FX-11J 46 (190°C/2.16 kg) 5.0 (23°C) 55.0 (屈服, ISO 527-1, -2) 25 (50 mm/min) 1.00E+16
LO-21A 8.60 (190°C/2.16 kg) 7.0 (23°C) 56.0 (屈服, ISO 527-1, -2) 40 (50 mm/min) 1.00E+16
WA-11H 25 (190°C/2.16 kg) 5.0 (23°C) 58.0 (屈服, ISO 527-1, -2) 21 (50 mm/min) 1.00E+16
FU2025 5.20 (190°C/2.16 kg) 19 (23°C) 39.0 (屈服, ISO 527-1, -2) > 100 (50 mm/min)
FU2050 3.90 (190°C/2.16 kg) 65 (23°C) 24.0 (屈服, ISO 527-1, -2) > 200 (50 mm/min)
ET-25 5.0 (23°C) 51.0 (屈服, ISO 527-1, -2) 10 (50 mm/min) 80
TC3015 4.0 (23°C) 54.0 (断裂, ISO 527-1, -2) 4.0 (5 mm/min) 8.30 (190°C/2.16 kg) 15 (Mineral)
TC3030 4.0 (23°C) 62.0 (断裂, ISO 527-1, -2) 3.0 (5 mm/min) 6.90 (190°C/2.16 kg) 30 (Mineral)
F20-55R2 7.70 (190°C/2.16 kg) 6.5 (23°C) 62.0 (屈服, ISO 527-1, -2) 30 (50 mm/min)
F20-73R1 7.90 (190°C/2.16 kg) 7.0 (23°C) 65.0 (屈服, ISO 527-1, -2) 30 (50 mm/min) 1.00E+16
F20-73R2 7.90 (190°C/2.16 kg) 7.0 (23°C) 63.0 (屈服, ISO 527-1, -2) 30 (50 mm/min) 1.00E+16
F30-73R1 23 (190°C/2.16 kg) 6.0 (23°C) 64.0 (屈服, ISO 527-1, -2) 26 (50 mm/min)
FU2010R2 6.00 (190°C/2.16 kg) 9.0 (23°C) 51.0 (屈服, ISO 527-1, -2) 50 (50 mm/min)
FU2020R2 5.80 (190°C/2.16 kg) 12 (23°C) 45.0 (屈服, ISO 527-1, -2) 65 (50 mm/min)
FX-11JR1 45 (190°C/2.16 kg) 5.0 (23°C) 55.0 (屈服, ISO 527-1, -2) 26 (50 mm/min)
FX-11R1 9.00 (190°C/2.16 kg) 7.0 (23°C) 55.0 (屈服, ISO 527-1, -2) 35 (50 mm/min)