| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 密度 | 1.08 g/cc | 0.0390 lb/in³ | DAM; ISO 1183 |
| 吸水率 | 6.7 % @Thickness 2.00 mm | 6.7 % @Thickness 0.0787 in | DAM; Sim. to ISO 62 |
| 水分吸收 | 2.20 % @Thickness 2.00 mm | 2.20 % @Thickness 0.0787 in | DAM; Sim. to ISO 62 |
| 线性成型收缩率,Flow | 0.017 cm/cm | 0.017 in/in | DAM; ISO 294-4 2577 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 抗张强度(屈服) | 43.0 MPa | 6240 psi | 50%RH; ISO 527-1/-2 |
| 50.0 MPa | 7250 psi | DAM; ISO 527-1/-2 | |
| 伸长率 (断裂) | 32 % | 32 % | DAM; Nominal; ISO 527-1/-2 |
| >= 50 % | >= 50 % | 50%RH; Nominal; ISO 527-1/-2 | |
| 屈服伸长率 | 5.7 % | 5.7 % | DAM; ISO 527-1/-2 |
| 37 % | 37 % | 50%RH; ISO 527-1/-2 | |
| 拉伸模量 | 0.900 GPa | 131 ksi | 50%RH; ISO 527-1/-2 |
| 2.00 GPa | 290 ksi | DAM; ISO 527-1/-2 | |
| 剪切模量 | 0.0822 GPa @Temperature 150 °C | 11.9 ksi @Temperature 302 °F | DAM; Dynamic; ISO 11403-1 -2 |
| 0.1075 GPa @Temperature 110 °C | 15.59 ksi @Temperature 230 °F | DAM; Dynamic; ISO 11403-1 -2 | |
| 0.2994 GPa @Temperature 60.0 °C | 43.42 ksi @Temperature 140 °F | DAM; Dynamic; ISO 11403-1 -2 | |
| 0.6815 GPa @Temperature 10.0 °C | 98.84 ksi @Temperature 50.0 °F | DAM; Dynamic; ISO 11403-1 -2 | |
| 0.7189 GPa @Temperature -20.0 °C | 104.3 ksi @Temperature -4.00 °F | DAM; Dynamic; ISO 11403-1 -2 | |
| 0.9346 GPa @Temperature -50.0 °C | 135.6 ksi @Temperature -58.0 °F | DAM; Dynamic; ISO 11403-1 -2 | |
| 简支梁无缺口冲击强度 | NB | NB | DAM; ISO 179/1eU |
| NB | NB | 50%RH; ISO 179/1eU | |
| NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | DAM; ISO 179/1eU | |
| NB @Temperature -30.0 °C | 50%RH; ISO 179/1eU | ||
| 简支梁缺口冲击强度 | 8.00 J/cm² | 38.1 ft-lb/in² | DAM; ISO 179/1eA |
| 11.5 J/cm² | 54.7 ft-lb/in² | 50%RH; ISO 179/1eA | |
| 1.70 J/cm² @Temperature -30.0 °C | 8.09 ft-lb/in² @Temperature -22.0 °F | 50%RH; ISO 179/1eA | |
| 1.80 J/cm² @Temperature -30.0 °C | 8.57 ft-lb/in² @Temperature -22.0 °F | DAM; ISO 179/1eA | |
| 拉伸蠕变模量(1 hr) | 1200 MPa @Time 3600 sec | 174000 psi @Time 1.00 hour | 50%RH; ISO 899-1 |
| 拉伸蠕变模量(1000 hr) | 750 MPa @Time 3.60e+6 sec | 109000 psi @Time 1000 hour | 50%RH; ISO 899-1 |
| 电气性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 体积电阻率 | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | 50%RH; IEC 60093 |
| 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | DAM; IEC 60093 | |
| 表面电阻 | >= 1.00e+15 ohm | >= 1.00e+15 ohm | 50%RH; IEC 60093 |
| 介电常数 | 2.9 @Frequency 1.00e+6 Hz | 2.9 @Frequency 1.00e+6 Hz | DAM; IEC 60250 |
| 3.2 @Frequency 100 Hz | 3.2 @Frequency 100 Hz | DAM; IEC 60250 | |
| 3.6 @Frequency 1.00e+6 Hz | 3.6 @Frequency 1.00e+6 Hz | 50%RH; IEC 60250 | |
| 8.0 @Frequency 100 Hz | 8.0 @Frequency 100 Hz | 50%RH; IEC 60250 | |
| 介电强度 | 31.0 kV/mm | 787 kV/in | DAM; IEC 60243-1 |
| 39.0 kV/mm | 991 kV/in | 50%RH; IEC 60243-1 | |
| 耗散因数 | 0.0080 @Frequency 100 Hz | 0.0080 @Frequency 100 Hz | DAM; IEC 60250 |
| 0.014 @Frequency 1.00e+6 Hz | 0.014 @Frequency 1.00e+6 Hz | DAM; IEC 60250 | |
| 0.055 @Frequency 1.00e+6 Hz | 0.055 @Frequency 1.00e+6 Hz | 50%RH; IEC 60250 | |
| 0.18 @Frequency 100 Hz | 0.18 @Frequency 100 Hz | 50%RH; IEC 60250 | |
| 相比耐漏电起痕指数(CTI) | 600 V | 600 V | DAM; IEC 60112 |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 线形热膨胀系数 - 流动 | 120 µm/m-°C | 66.7 µin/in-°F | DAM; ISO 11359-1/-2 |
| 线性热膨胀系数,横向流动 | 90.0 µm/m-°C | 50.0 µin/in-°F | DAM; ISO 11359-1/-2 |
| 熔融温度 | 263 °C | 505 °F | DAM; 10°C/min; ISO 11357-1/-3 |
| 载荷下热变形温度(0.46 MPa) | 132 °C | 270 °F | DAM; ISO 75-1/-2 |
| 载荷下热变形温度(1.8 MPa) | 64.0 °C | 147 °F | DAM; ISO 75-1/-2 |
| 玻璃化转变温度，Tg | 75.0 °C | 167 °F | DAM; 10°C/min; ISO 11357-1/-2 |
| 可燃性(UL94) | HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | DAM; IEC 60695-11-10 |
| HB @Thickness 0.800 mm | HB @Thickness 0.0315 in | DAM; IEC 60695-11-10 | |
| Flame Spread | 26 mm/min @Thickness 1.00 mm | 1.0 in/min @Thickness 0.0394 in | ISO 3795 (FMVSS 302) |
| 极限氧指数 | 20 % | 20 % | DAM; ISO 4589-1/-2 |
| 材料描述 | 测试方法 | |
|---|---|---|
| Emission of organic compounds | 38.4 µgC/g | VDA 277 |
| Odour | class 3 | VDA 270 |
| 部件标识代码 | >PA66-HI< | ISO 11469 |
| 加工 | Injection Moulding | |
| Other Extrusion | ||
| 供货地区 | Europe | |
| Near East/Africa | ||
| 树脂识别 | PA66-HI |