107 物性表
其它性能额定值单位测试方法弯曲降服强度 (+73℉)14.3MPsiASTM D-790基本性能额定值单位测试方法密度1.42ASTM D-792物理性能额定值单位测试方法吸水量
ASTM D-570 (Equil.50%R.h.+73℉(+23℃))0.22%
(24hrs浸泡+73℉(+23℃))0.25%
(浸泡均衡点+73℉(+23℃))0.90%
扩散因数 (+73℉(+23℃)10Hz)0.005
ASTM D-150机械性能额定值单位测试方法摩擦系数 (+73℉(+23℃)动态)0.35
ThrustWasherTest挠曲系数
在25℃下 (+70℃)1550MPa
(-55℃)3650MPa
断裂时之拉力伸张度 (+73℉(+23℃))75%ASTM D-638挠曲系数 (+158℉)225MPsi在25℃下伸张强度 (+212℉)5.2MPsiASTM D-638断裂时之拉力伸张度 (+212℉(+100℃))>260%ASTM D-638IZOD冲击强度 (+73℉)2.3ft.lb/inASTM D-256伸张强度
ASTM D-638 (+250℉)3.8MPsi
(-68℉)14.7MPsi
挠曲系数
在25℃下 (+212℉)130MPsi
(-68℉)530MPsi
(+250℉)90MPsi
拉力冲击抵抗力
D1822Long (+73℉)170ft.lb/in
(+23℃)350kj/m
剪力 (+23℃)65.5MPaASTM D-732挠曲系数 (+73℉)380MPsi在25℃下剪力 (+73℉)9.5MPsiASTM D-732挠曲系数 (+100℃)895MPa25℃下弯曲疲劳忍耐限度 (+73℉)4.7MPsiASTM D-671伸张强度 (+100℃)35.9MPaASTM D-638断裂时之拉力伸张度
ASTM D-638 (+250℉(+122℃))>260%
(+158℉(+70℃))230%
无切口冲击程度 (+73℉)>100(no break)ft.lb/inASTM D-256弯曲降服强度 (+23℃)98.6MPaASTM D-790压缩应力 (+23℃@1%Def.)35.9MPaASTM D-695伸张强度 (-55℃)101MPaASTM D-638挠曲系数 (+23℃)2620MPa在25℃下伸张强度 (+73℉)10.0MPsiASTM D-638压缩应力 (+73℉@10%Def)18.0MPsiASTM D-695伸张强度 (+122℃)26.2MPaASTM D-638压缩应力 (+23℃@10%Def.)124MPaASTM D-695伸张强度 (+70℃)6.9MPaASTM D-638弯曲疲劳忍耐限度 (+23℃)32.4MPaASTM D-671IZOD冲击强度 (40℃)96.1j/mASTM D-256伸张强度 (+158℉)6.9MPsiASTM D-638IZOD冲击强度 (-40℉)1.8ft.lb/inASTM D-256洛氏硬度M94,R120
ASTM D-785挠曲系数 (+122℃)620MPa在25℃下弹性系数 (+73℉)450MPsiASTM D-638摩擦系数 (+73℉(+23℃)静态)0.20
ThrustWasherTest弹性系数 (+23℃)3100MPaASTM D-638断裂时之拉力伸张度 (-68℉(-55℃))38%ASTM D-638负载下之变形 (2000psi@+122℉(14Mpa@50℃))0.5%ASTM D-621伸张强度 (+23℃)68.9MPaASTM D-638无切口冲击程度 (+23℃)>5300(no break)j/mASTM D-256IZOD冲击强度 (+23℃)123j/mASTM D-256压缩应力 (+73℉@1%Def.)5.2MPsiASTM D-695电气性能额定值单位测试方法绝缘强度 (Short Time,2.3mm)19.7MV/mASTM D-149绝缘系数 (+73℉(+23℃)10to10Hz)3.7
ASTM D-150电弧抵抗力 (120mil(3.1mm))220no trackingSec.ASTM D-495绝缘强度 (Short Time,90 mils)500V/milASTM D-149电阻系数 (+73℉(+23℃)0.2%H2O)10ohm-cmASTM D-257热性能额定值单位测试方法可燃烧性94HB
UL-94线性热膨胀系数
ASTM D-696 (-40 to +85℉)5.810-5in/in.℉
(+220 to +300℉)8.310-5in/in.℉
热变形温度 (0.5MPa)172℃ASTM D-648线性热膨胀系数 (-40 to +29℃)10.410-5m/m.℃ASTM D-696热传导系数2.6BTU-in/hr
线性热膨胀系数 (+60 to +104℃)13.710-5m/m.℃ASTM D-696热变形温度
ASTM D-648 (1.8MPa)136℃
(66psi)342℉
熔点175℃ASTM D-2133热变形温度 (264psi)277℉ASTM D-648熔点347℉ASTM D-2133线性热膨胀系数
ASTM D-696 (+29 to +60℃)12.210-5m/m.℃
(+104 to +150℃)14.910-5m/m.℃
(+85 to +140℉)6.810-5in/in.℉
(+140 to +220℉)7.610-5in/in.℉
热传导系数0.37W/mk