规格参数：
| 规格 : | φ10mm-φ300mm | 产地/厂家 : | 攀长钢 |
| 材质 : | 50Mn18Cr4N |
50Mn18Cr4N无磁性奥氏体护环钢 φ10
50Mn18Cr4N汽轮发电机无磁性护环锻件50Mn18Cr4N无磁性奥氏体护环钢 φ16 50Mn18Cr4N汽轮发电机无磁性护环锻件50Mn18Cr4N无磁性奥氏体护环钢 φ20 50Mn18Cr4N汽轮发电机无磁性护环锻件50Mn18Cr4N无磁性奥氏体护环钢 φ26 50Mn18Cr4N汽轮发电机无磁性护环锻件50Mn18Cr4N无磁性奥氏体护环钢 φ30 50Mn18Cr4N汽轮发电机无磁性护环锻件50Mn18Cr4N无磁性奥氏体护环钢 φ32 50Mn18Cr4N汽轮发电机无磁性护环锻件50Mn18Cr4N无磁性奥氏体护环钢 φ36 50Mn18Cr4N汽轮发电机无磁性护环锻件50Mn18Cr4N无磁性奥氏体护环钢 φ40 50Mn18Cr4N汽轮发电机无磁性护环锻件50Mn18Cr4N无磁性奥氏体护环钢 φ45 50Mn18Cr4N汽轮发电机无磁性护环锻件50Mn18Cr4N无磁性奥氏体护环钢 φ50 50Mn18Cr4N汽轮发电机无磁性护环锻件
50Mn18Cr4N无磁性奥氏体护环钢 φ55
50Mn18Cr4N汽轮发电机无磁性护环锻件50Mn18Cr4N无磁性奥氏体护环钢 φ60 50Mn18Cr4N汽轮发电机无磁性护环锻件50Mn18Cr4N无磁性奥氏体护环钢 φ65 50Mn18Cr4N汽轮发电机无磁性护环锻件50Mn18Cr4N无磁性奥氏体护环钢 φ70 50Mn18Cr4N汽轮发电机无磁性护环锻件50Mn18Cr4N无磁性奥氏体护环钢 φ75 50Mn18Cr4N汽轮发电机无磁性护环锻件
50Mn18Cr4N无磁性奥氏体护环钢 φ80
50Mn18Cr4N汽轮发电机无磁性护环锻件======================上海高高商贸有限公司：电话：
021-36308863手机：
18917081101QQ:404914802联系人：粟太成地址：上海市宝山区抚远路1288弄61号==================================材料名称：锰铬系无磁性奥氏体护环钢牌号：
50Mn18Cr4N标准：JB 1268-1993特性及适用范围：是锰铬系无磁性奥氏体护环钢，在 50Mn18Cr4的基础上加氮而得到。
氮能扩大和稳定奥氏体，使钢强化。
固溶处理后，进行半热变形强化或冷变形强化以满足不同类别的强度要求。
用于汽轮发电机无磁性护环锻件及其他要求无磁性的零部件。
力学性能：抗拉强度 σb (MPa)：I级,≥895条件屈服强度 σ0.2 (MPa)：I级,≥760伸长率 δ5 (％)：I级,≥25断面收缩率 ψ (％)：I级,≥35化学成份：碳 C ：0.40～0.60硅 Si：0.30～0.80锰 Mn：17.00～19.00硫 S ：≤0.025磷 P ：≤0.080铬 Cr：3.00～5.00氮 N ：0.08～0.12热处理规范及金相组织：热处理规范：1)热成形后和变形强化前固溶处理;2)变形强化后以≤40℃h的速率,加热到320～350℃,保温8～12h,以≤40℃h速率缓冷至100℃以下,以消除残余应力。
50Mn18Cr4N无磁钢以上由上海高高特钢自行发行，如有对50Mn18Cr4N无磁钢不详之处，敬请来电洽谈！高高特钢将以真信息、真品质、真价格的为您提供