商品描述价格说明联系我们品牌日本杜邦是否支持加工定制是规格25KG/包加工方式注射成型颜色本色/黑色原料形状颗粒状中文名称聚对苯二甲酸乙二醇酯分类工程塑料包装原厂原包销售方式品牌经销应用电动工具、汽车部件、电子电器等。
备注实际售价以当日咨询报价为准。
供货方式现货可售卖地全国类型标准料型号FR530 BK507DuPont Performance Polymers Rynite® FR530 BK507 PET (Unverified Data**)Polyethylene Terephthalate (PET), 30% Glass ReinforcedDuPont Performance Polymers产品说明：Rynite® FR530 BK507 is a 30% glass reinforced, flame retardant, modified polyethylene terephthalate resin.Information provided by DuPont Performance Polymers物性信息：物理性能额定值 (公制)额定值 (英制)测试方法密度1.68 g/cc0.0607 lb/in³ISO 1183填料含量30 %30 %线性成型收缩率,Flow0.0020 cm/cm@Thickness 2.00 mm0.0020 in/in@Thickness 0.0787 inISO 294-4线性成型收缩率，横向0.0080 cm/cm@Thickness 2.00 mm0.0080 in/in@Thickness 0.0787 inISO 294-4机械性能额定值 (公制)额定值 (英制)测试方法抗张强度(断裂)43.0 MPa@Temperature 150 °C6240 psi@Temperature 302 °FISO 52767.0 MPa@Temperature 90.0 °C9720 psi@Temperature 194 °FISO 527130 MPa@Temperature 23.0 °C18900 psi@Temperature 73.4 °FISO 527172 MPa@Temperature -40.0 °C24900 psi@Temperature -40.0 °FISO 527伸长率 (断裂)1.8 %@Temperature -40.0 °C1.8 %@Temperature -40.0 °FISO 5271.9 %@Temperature 23.0 °C1.9 %@Temperature 73.4 °FISO 5273.5 %@Temperature 90.0 °C3.5 %@Temperature 194 °FISO 5274.0 %@Temperature 150 °C4.0 %@Temperature 302 °FISO 527拉伸模量3.65 GPa@Temperature 150 °C529 ksi@Temperature 302 °FISO 5275.90 GPa@Temperature 90.0 °C856 ksi@Temperature 194 °FISO 52711.3 GPa@Temperature 23.0 °C1640 ksi@Temperature 73.4 °FISO 52712.0 GPa@Temperature -40.0 °C1740 ksi@Temperature -40.0 °FISO 527弯曲强度69.0 MPa@Temperature 150 °C10000 psi@Temperature 302 °FISO 178107 MPa@Temperature 90.0 °C15500 psi@Temperature 194 °FISO 178200 MPa@Temperature 23.0 °C29000 psi@Temperature 73.4 °FISO 178262 MPa@Temperature -40.0 °C38000 psi@Temperature -40.0 °FISO 178弯曲模量2.65 GPa@Temperature 150 °C384 ksi@Temperature 302 °FISO 1784.65 GPa@Temperature 90.0 °C674 ksi@Temperature 194 °FISO 17810.5 GPa@Temperature 23.0 °C1520 ksi@Temperature 73.4 °FISO 17811.0 GPa@Temperature -40.0 °C1600 ksi@Temperature -40.0 °FISO 178悬壁梁缺口冲击强度8.00 kJ/m²@Temperature -40.0 °C3.81 ft-lb/in²@Temperature -40.0 °FISO 180/1A8.00 kJ/m²@Temperature -30.0 °C3.81 ft-lb/in²@Temperature -22.0 °FISO 180/1A8.50 kJ/m²@Temperature 23.0 °C4.04 ft-lb/in²@Temperature 73.4 °FISO 180/1A悬壁梁无缺口冲击强度34.0 kJ/m²@Temperature -40.0 °C16.2 ft-lb/in²@Temperature -40.0 °FISO 180/1U35.0 kJ/m²@Temperature -30.0 °C16.7 ft-lb/in²@Temperature -22.0 °FISO 180/1U40.0 kJ/m²@Temperature 23.0 °C19.0 ft-lb/in²@Temperature 73.4 °FISO 180/1U简支梁无缺口冲击强度3.00 J/cm²@Temperature -40.0 °C14.3 ft-lb/in²@Temperature -40.0 °FISO 179/1eU3.50 J/cm²@Temperature -30.0 °C16.7 ft-lb/in²@Temperature -22.0 °FISO 179/1eU4.00 J/cm²@Temperature 23.0 °C19.0 ft-lb/in²@Temperature 73.4 °FISO 179/1eU简支梁缺口冲击强度0.800 J/cm²@Temperature -40.0 °C3.81 ft-lb/in²@Temperature -40.0 °FISO 179/1eA0.800 J/cm²@Temperature -30.0 °C3.81 ft-lb/in²@Temperature -22.0 °FISO 179/1eA0.900 J/cm²@Temperature 23.0 °C4.28 ft-lb/in²@Temperature 73.4 °FISO 179/1eA电气性能额定值 (公制)额定值 (英制)测试方法Comparative Tracking Index225 V@Temperature 23.0 °C225 V@Temperature 73.4 °FIEC 60112250 V@Temperature 23.0 °C250 V@Temperature 73.4 °FUL 746A250 - 400 V@Temperature 23.0 °C250 - 400 V@Temperature 73.4 °FUL 746A热性能额定值 (公制)额定值 (英制)测试方法线形热膨胀系数 - 流动500 µm/m-°C@Temperature -40.0 - 23.0 °C278 µin/in-°F@Temperature -40.0 - 73.4 °FISO 11359-1/-2500 µm/m-°C@Temperature 23.0 - 55.0 °C278 µin/in-°F@Temperature 73.4 - 131 °FISO 11359-1/-2500 µm/m-°C@Temperature 55.0 - 160 °C278 µin/in-°F@Temperature 131 - 320 °FISO 11359-1/-2线性热膨胀系数,横向流动73.0 µm/m-°C@Temperature -40.0 - 23.0 °C40.6 µin/in-°F@Temperature -40.0 - 73.4 °FISO 11359-1/-290.0 µm/m-°C@Temperature 23.0 - 55.0 °C50.0 µin/in-°F@Temperature 73.4 - 131 °FISO 11359-1/-2121 µm/m-°C@Temperature 55.0 - 160 °C67.2 µin/in-°F@Temperature 131 - 320 °FISO 11359-1/-2熔融温度252 °C486 °F10°C/min; ISO 11357-1/-3载荷下热变形温度(0.46 MPa)243 °C469 °FISO 75-1/-2载荷下热变形温度(1.8 MPa)220 °C428 °FISO 75-1/-2UL RTI155 °C@Thickness 0.350 mm311 °F@Thickness 0.0138 inUL 746B155 °C@Thickness 0.750 mm311 °F@Thickness 0.0295 inUL 746B155 °C@Thickness 1.50 mm311 °F@Thickness 0.0591 inUL 746B155 °C@Thickness 2.00 mm311 °F@Thickness 0.0787 inUL 746B155 °C@Thickness 3.00 mm311 °F@Thickness 0.118 inUL 746BUL RTI，机械冲击155 °C@Thickness 2.00 mm311 °F@Thickness 0.0787 inUL 746B155 °C@Thickness 3.00 mm311 °F@Thickness 0.118 inUL 746B155 °C@Thickness 1.50 mm311 °F@Thickness 0.0591 inUL 746B155 °C@Thickness 0.750 mm311 °F@Thickness 0.0295 inUL 746BUL RTI，机械无冲击155 °C@Thickness 0.750 mm311 °F@Thickness 0.0295 inUL 746B155 °C@Thickness 1.50 mm311 °F@Thickness 0.0591 inUL 746B155 °C@Thickness 2.00 mm311 °F@Thickness 0.0787 inUL 746B155 °C@Thickness 3.00 mm311 °F@Thickness 0.118 inUL 746B可燃性(UL94)V-0@Thickness 2.00 mmV-0@Thickness 0.0787 inUL94V-0@Thickness 1.50 mmV-0@Thickness 0.0591 inUL94V-0@Thickness 0.750 mmV-0@Thickness 0.0295 inUL94V-0@Thickness 0.350 mmV-0@Thickness 0.0138 inUL94