PET日本杜邦530 NC

商品描述价格说明联系我们牌号530NC厂商日本杜邦销售方式品牌经销用途级别汽车部件，通用级塑料种类聚对苯二甲酸乙二酯加工级别注塑级，吹塑级特性级别耐高温，阻燃级，热稳定性规格25公斤颜色本色可售卖地全国材质PET薄膜类型标准料DuPont Performance Polymers Rynite® 530 NC010 Polyethylene Terephthalate (PET) (Unverified Data**)Polyethylene Terephthalate (PET), 30% Glass ReinforcedDuPont Performance Polymers产品说明：30% Glass Reinforced Polyethylene TerephthalateRynite 530 NC010 is a 30% glass fiber reinforced modified polyethylene terephthalate resin with an outstanding balance of strength stiffness and toughness excellent electrical properties surface appearancInformation provided by DuPont Performance Polymers物性信息：物理性能额定值 (公制)额定值 (英制)测试方法比重1.56 g/cc1.56 g/ccASTM D792密度1.56 g/cc0.0564 lb/in³ISO 1183吸水率0.70 %@Thickness 2.00 mm0.70 %@Thickness 0.0787 inSim. to ISO 62水分吸收0.200 %@Thickness 2.00 mm0.200 %@Thickness 0.0787 inSim. to ISO 62粘度44000 cP@Shear Rate 5000 1/s, Temperature 300 °C44000 cP@Shear Rate 5000 1/s, Temperature 572 °FISO 11403-1 -260000 cP@Shear Rate 5000 1/s, Temperature 290 °C60000 cP@Shear Rate 5000 1/s, Temperature 554 °FISO 11403-1 -282000 cP@Shear Rate 5000 1/s, Temperature 280 °C82000 cP@Shear Rate 5000 1/s, Temperature 536 °FISO 11403-1 -2130000 cP@Shear Rate 500 1/s, Temperature 300 °C130000 cP@Shear Rate 500 1/s, Temperature 572 °FISO 11403-1 -2174000 cP@Shear Rate 500 1/s, Temperature 290 °C174000 cP@Shear Rate 500 1/s, Temperature 554 °FISO 11403-1 -2232000 cP@Shear Rate 500 1/s, Temperature 280 °C232000 cP@Shear Rate 500 1/s, Temperature 536 °FISO 11403-1 -2线性成型收缩率,Flow0.0020 cm/cm0.0020 in/inISO 294-4 2577线性成型收缩率，横向0.0080 cm/cm0.0080 in/inISO 294-4 2577熔体流动速率5.0 g/10 min@Load 2.16 kg, Temperature 280 °C5.0 g/10 min@Load 4.76 lb, Temperature 536 °Fcm³/10min; ISO 1133机械性能额定值 (公制)额定值 (英制)测试方法洛氏硬度（M 级）100100ISO 2039-2洛氏硬度（R 级）120120ISO 2039-2抗张强度(断裂)158 MPa22900 psiISO 527-1/-2抗张强度16.7 MPa@Strain 0.460 %, Temperature 150 °C2420 psi@Strain 0.460 %, Temperature 302 °FISO 11403-1 -223.95 MPa@Strain 0.490 %, Temperature 90.0 °C3474 psi@Strain 0.490 %, Temperature 194 °FISO 11403-1 -225.5 MPa@Strain 0.260 %, Temperature 40.0 °C3700 psi@Strain 0.260 %, Temperature 104 °FISO 11403-1 -227.0 MPa@Strain 0.250 %, Temperature 23.0 °C3920 psi@Strain 0.250 %, Temperature 73.4 °FISO 11403-1 -227.4 MPa@Strain 0.240 %, Temperature 0.000 °C3970 psi@Strain 0.240 %, Temperature 32.0 °FISO 11403-1 -228.9 MPa@Strain 0.230 %, Temperature -40.0 °C4190 psi@Strain 0.230 %, Temperature -40.0 °FISO 11403-1 -245.0 MPa@Strain 1.84 %, Temperature 150 °C6530 psi@Strain 1.84 %, Temperature 302 °FISO 11403-1 -257.0 MPa@Strain 3.21 %, Temperature 150 °C8270 psi@Strain 3.21 %, Temperature 302 °FISO 11403-1 -262.0 MPa@Strain 4.59 %, Temperature 150 °C8990 psi@Strain 4.59 %, Temperature 302 °FISO 11403-1 -262.15 MPa@Strain 1.90 %, Temperature 90.0 °C9014 psi@Strain 1.90 %, Temperature 194 °FISO 11403-1 -278.2 MPa@Strain 3.30 %, Temperature 90.0 °C11300 psi@Strain 3.30 %, Temperature 194 °FISO 11403-1 -282.65 MPa@Strain 4.71 %, Temperature 90.0 °C11990 psi@Strain 4.71 %, Temperature 194 °FISO 11403-1 -282.95 MPa@Strain 1.04 %, Temperature 40.0 °C12030 psi@Strain 1.04 %, Temperature 104 °FISO 11403-1 -290.0 MPa@Strain 0.970 %, Temperature 23.0 °C13100 psi@Strain 0.970 %, Temperature 73.4 °FISO 11403-1 -297.0 MPa@Strain 0.950 %, Temperature 0.000 °C14100 psi@Strain 0.950 %, Temperature 32.0 °FISO 11403-1 -2105 MPa@Strain 0.940 %, Temperature -40.0 °C15200 psi@Strain 0.940 %, Temperature -40.0 °FISO 11403-1 -2117.1 MPa@Strain 1.82 %, Temperature 40.0 °C16980 psi@Strain 1.82 %, Temperature 104 °FISO 11403-1 -2131.5 MPa@Strain 2.60 %, Temperature 40.0 °C19070 psi@Strain 2.60 %, Temperature 104 °FISO 11403-1 -2134 MPa@Strain 1.69 %, Temperature 23.0 °C19400 psi@Strain 1.69 %, Temperature 73.4 °FISO 11403-1 -2151 MPa@Strain 1.67 %, Temperature 0.000 °C21900 psi@Strain 1.67 %, Temperature 32.0 °FISO 11403-1 -2155 MPa@Strain 2.42 %, Temperature 23.0 °C22500 psi@Strain 2.42 %, Temperature 73.4 °FISO 11403-1 -2164 MPa@Strain 1.60 %, Temperature -40.0 °C23800 psi@Strain 1.60 %, Temperature -40.0 °FISO 11403-1 -2185 MPa@Strain 2.38 %, Temperature 0.000 °C26800 psi@Strain 2.38 %, Temperature 32.0 °FISO 11403-1 -2211 MPa@Strain 2.29 %, Temperature -40.0 °C30600 psi@Strain 2.29 %, Temperature -40.0 °FISO 11403-1 -220.0 MPa@Strain 0.222 %, Time 3.60e+6 sec2900 psi@Strain 0.222 %, Time 1000 hourisochronous; ISO 11403-1 -220.0 MPa@Strain 0.190 %, Time 36000 sec2900 psi@Strain 0.190 %, Time 10.0 hourisochronous; ISO 11403-1 -220.0 MPa@Strain 0.201 %, Time 360000 sec2900 psi@Strain 0.201 %, Time 100 hourisochronous; ISO 11403-1 -220.0 MPa@Strain 0.247 %, Time 1.80e+7 sec2900 psi@Strain 0.247 %, Time 5000 hourisochronous; ISO 11403-1 -220.0 MPa@Strain 0.260 %, Time 3.60e+7 sec2900 psi@Strain 0.260 %, Time 10000 hourisochronous; ISO 11403-1 -220.0 MPa@Strain 0.183 %, Time 3600 sec2900 psi@Strain 0.183 %, Time 1.00 hourisochronous; ISO 11403-1 -260.0 MPa@Strain 0.574 %, Time 3600 sec8700 psi@Strain 0.574 %, Time 1.00 hourisochronous; ISO 11403-1 -260.0 MPa@Strain 0.831 %, Time 3.60e+7 sec8700 psi@Strain 0.831 %, Time 10000 hourisochronous; ISO 11403-1 -260.0 MPa@Strain 0.785 %, Time 1.80e+7 sec8700 psi@Strain 0.785 %, Time 5000 hourisochronous; ISO 11403-1 -260.0 MPa@Strain 0.638 %, Time 360000 sec8700 psi@Strain 0.638 %, Time 100 hourisochronous; ISO 11403-1 -260.0 MPa@Strain 0.599 %, Time 36000 sec8700 psi@Strain 0.599 %, Time 10.0 hourisochronous; ISO 11403-1 -260.0 MPa@Strain 0.709 %, Time 3.60e+6 sec8700 psi@Strain 0.709 %, Time 1000 hourisochronous; ISO 11403-1 -2伸长率 (断裂)2.5 %2.5 %ISO 527-1/-2拉伸模量11.0 GPa1600 ksiISO 527-1/-2弯曲强度230 MPa33400 psiISO 178弯曲模量8.95 GPa1300 ksiISO 178剪切模量0.548 GPa@Temperature 160 °C79.5 ksi@Temperature 320 °FDynamic; ISO 11403-1 -20.637 GPa@Temperature 120 °C92.4 ksi@Temperature 248 °FDynamic; ISO 11403-1 -21.33 GPa@Temperature 70.0 °C193 ksi@Temperature 158 °FDynamic; ISO 11403-1 -22.101 GPa@Temperature 20.0 °C304.7 ksi@Temperature 68.0 °FDynamic; ISO 11403-1 -22.288 GPa@Temperature -20.0 °C331.9 ksi@Temperature -4.00 °FDynamic; ISO 11403-1 -22.487 GPa@Temperature -50.0 °C360.7 ksi@Temperature -58.0 °FDynamic; ISO 11403-1 -2抗剪强度0.0650 MPa@Shear Rate 500 1/s, Temperature 300 °C9.43 psi@Shear Rate 500 1/s, Temperature 572 °FISO 11403-1 -20.0870 MPa@Shear Rate 500 1/s, Temperature 290 °C12.6 psi@Shear Rate 500 1/s, Temperature 554 °FISO 11403-1 -20.116 MPa@Shear Rate 500 1/s, Temperature 280 °C16.8 psi@Shear Rate 500 1/s, Temperature 536 °FISO 11403-1 -2割线模量5.97 GPa@Strain 2.08 %, Temperature 40.0 °C865 ksi@Strain 2.08 %, Temperature 104 °FISO 11403-1 -2