Polyphenylene Sulfide
Celanese Corporation
40% 玻璃纤维增强材料
产品说明：
Fortron 1140L4 is a 40% glass-reinforced grade that is the strongest and toughest product available. It exhibits excellent heat and chemical resistance, good electrical properties and is inherently flame-retardant. The high hardness and rigidity at elevated temperatures allows for good load bearing performance. This product has good weldability due to the modest filler level. Applications made of this grade are electronical components (i.e. bobbins, lamp housings, brush holders) and various other components requiring strength and resistance to aggressive chemicals (i.e. automotive heaters, pumps, valves, fuel rails, microwave oven rings and distillation column packings).
物性信息：
基本信息黄卡编号
E107854-237735
E107854-237738
E107854-237739
填料/增强材料玻璃纤维增强材料, 40% 填料按重量
特性超高韧性
刚性，高
高强度
可焊接
良好的电气性能
耐化学性良好
耐热性，高
硬度高
阻燃性
用途泵件
电气/电子应用领域
阀门/阀门部件
汽车领域的应用
外壳
RoHS 合规性联系制造商
多点数据Isochronous Stress vs. Strain (ISO 11403-1)
Isothermal Stress vs. Strain (ISO 11403-1)
Shear Modulus vs. Temperature (ISO 11403-1)
物理性能额定值单位制测试方法比重1.65g/cm³ASTM D792, ISO 1183特定体积0.611cm³/gASTM D792充模分析额定值单位制测试方法Specific Heat Capacity of Melt1500J/kg/°C内部方法补充信息额定值单位制测试方法Specimen Thickness - Shrinkage3.18mm内部方法物理性能额定值单位制测试方法收缩率流动0.20 到 0.30%ASTM D955 横向流动0.50 到 0.70%ASTM D955 垂直流动方向0.40 到 0.60%ISO 294-4 流动方向0.20 到 0.60%ISO 294-4吸水率 (饱和, 23°C)0.020%ISO 62硬度额定值单位制测试方法洛氏硬度
M 级100
ASTM D785 M 计秤100
ISO 2039-2机械性能额定值单位制测试方法拉伸模量
-40°C14500MPaASTM D638 75°C11900MPaASTM D638 150°C4270MPaASTM D638 200°C3240MPaASTM D638 --14700MPaISO 527-2/1A/1抗张强度
断裂, 23°C200MPaASTM D638 断裂195MPaISO 527-2/1A/5伸长率
断裂, 23°C1.7%ASTM D638 断裂1.9%ISO 527-2/1A/5弯曲模量 (23°C)14500MPaISO 178弯曲应力 1285MPaISO 178冲击性能额定值单位制测试方法简支梁缺口冲击强度
ISO 179/1eA -30°C10kJ/m²ISO 179/1eA 23°C10kJ/m²ISO 179/1eA简支梁无缺口冲击强度
ISO 179/1eU -30°C53kJ/m²ISO 179/1eU 23°C53kJ/m²ISO 179/1eU悬壁梁缺口冲击强度
ISO 180/1A -30°C10kJ/m²ISO 180/1A 23°C10kJ/m²ISO 180/1A无缺口伊佐德冲击强度 (23°C)34kJ/m²ISO 180/1U热性能额定值单位制测试方法载荷下热变形温度
0.45 MPa, 退火280°CASTM D648 1.8 MPa, 未退火265°CASTM D648 1.8 MPa, 未退火270°CISO 75-2/A 8.0 MPa, 未退火215°CISO 75-2/C玻璃转化温度 290.0°CISO 11357-2熔融温度 3280°CISO 11357-3线形热膨胀系数
ISO 11359-2 流动2.6E-5cm/cm/°CISO 11359-2 横向4.2E-5cm/cm/°CISO 11359-2电气性能额定值单位制测试方法表面电阻率> 1.0E+15ohmsIEC 60093体积电阻率
--1.0E+16ohms·cmASTM D257 --> 1.0E+15ohms·cmIEC 60093介电强度28kV/mmIEC 60243-1介电常数
1 kHz3.50
ASTM D150 1 MHz3.50
ASTM D150 1 MHz4.60
IEC 60250耗散因数
1 kHz1.0E-3
ASTM D150 1 MHz1.0E-3
ASTM D150 1 MHz6.2E-3
IEC 60250耐电弧性134secASTM D495漏电起痕指数125VIEC 60112可燃性额定值单位制测试方法UL 阻燃等级
UL 94 0.380 mmV-0
UL 94 1.50 mmV-0
UL 94 3.00 mm5VA
UL 94极限氧指数47%ISO 4589-2注射额定值单位制
干燥温度130 到 140°C
干燥时间3.0 到 4.0hr
建议的最大水分含量0.020%
料斗温度20.0 到 30.0°C
料筒后部温度290 到 300°C
料筒中部温度310 到 320°C
料筒前部温度330 到 340°C
射嘴温度310 到 330°C
加工（熔体）温度330 到 340°C
模具温度140 到 160°C
注塑压力50.0 到 100MPa
注射速度快速
保压30.0 到 70.0MPa
背压0.00 到 3.00MPa
注射说明