Generic Name: 聚偏二氟乙烯 (PVDF) - 提供方: Arkema High Performance Polymers
Kynar Flex® resins are fluorinated thermoplastic copolymers.
Outstanding characteristics: chemical resistance, imperviousness to UV, high barrier properties, high purity, good mechanical and thermo-mechanical properties.
Kynar Flex® 2800-00 resin is a standard grade of granules, compared to the homopolymer grades, which exhibits a lower modulus, a better resistance to stress cracking in alkaline and oxidizing media, and a lower melting point.
For cable coating, extrusion of tube and plaque, compression molding of bulky parts.
Additional characteristics:
Easily processed using conventional equipment
Excellent thermal stability
Retains properties after aging
Pigmentable
UL RTI temperature rating 125ºC
Radiation crosslinking
与典型值比较 - Upgrade to compare! 与黄卡比较
单位: SI
总览
材料状态
已商用：当前有效
资料 1Technical Datasheet (English)
UL 黄卡 2E54699-244851
搜索 UL 黄卡Arkema High Performance Polymers
供货地区北美洲
非洲和中东
拉丁美洲
欧洲
亚太地区
添加剂热稳定剂
紫外线稳定剂
特性Good ESCR (Stress Crack Resist.)
纯度高
辐射可交联
共聚物
光稳定
可交联
良好的加工性能
良好的着色性
耐化学品性能，良好
耐热老化性能，良好
耐紫外光性能，良好
热稳定性
热稳定性，良好
阻隔树脂
用途电缆护套
电线电缆应用
管件
涂层应用
型材
形式颗粒
粒子
加工方法挤出
涂层
型材挤出成型
压缩模塑
多点数据Isothermal Stress vs. Strain (ISO 11403)
Secant Modulus vs. Strain (ISO 11403)
Shear Modulus vs. Temperature (ISO 11403)
Viscosity vs. Shear Rate (ISO 11403)
物理性能额定值
单位制
测试方法
密度 / 比重-- 4
1.77 到 1.80
g/cm³
ASTM D792--1.78
g/cm³
ISO 1183熔流率（熔体流动速率） (230°C/12.5 kg)3.0 到 8.0
g/10 min
ASTM D1238熔融体积流量（MVR） (230°C/5.0 kg)0.50
cm³/10min
ISO 1133吸水率饱和
0.030 到 0.050
%
ASTM D570饱和, 23°C0.030
%
ISO 62平衡, 23°C, 50% RH0.015
%
ISO 62机械性能额定值
单位制
测试方法
拉伸模量23°C
552 到 896
MPa
ASTM D638--700
MPa
ISO 527-1抗张强度屈服, 23°C
20.0 到 34.5
MPa
ASTM D638屈服27.0
MPa
ISO 527-2断裂, 23°C17.2 到 34.5
MPa
ASTM D638伸长率屈服, 23°C
10 到 20
%
ASTM D638屈服15
%
ISO 527-2断裂, 23°C100 到 300
%
ASTM D638标称拉伸断裂应变> 50
%
ISO 527-2弯曲模量 (23°C)483 到 758
MPa
ASTM D790弯曲强度 (5.0% 应变, 23°C)20.7 到 34.5
MPa
ASTM D790压缩强度 (23°C)31.0 到 41.4
MPa
ASTM D695摩擦系数 4ASTM D1894与钢 - 动态
0.33
与钢 - 静态
0.33
泰伯耐磨性 (1000 Cycles, 1000 g, CS-17 转轮)
16.0 到 19.0
mg
内部方法冲击性能额定值
单位制
测试方法
简支梁缺口冲击强度ISO 179/1eA-30°C
5.0
kJ/m²
23°C
无断裂
悬壁梁缺口冲击强度 (23°C)
530 到 1100
J/m
ASTM D256无缺口悬臂梁冲击 (23°C)无断裂
ASTM D256硬度
额定值
单位制
测试方法
肖氏硬度 (邵氏 D, 23°C)60 到 70
ASTM D2240热性能
额定值
单位制
测试方法
载荷下热变形温度0.45 MPa, 未退火 5
60.0 到 75.0
°C
ASTM D6480.45 MPa, 未退火38.0
°C
ISO 75-2/B1.8 MPa, 未退火 540.0 到 55.0
°C
ASTM D6481.8 MPa, 未退火48.0
°C
ISO 75-2/A玻璃转化温度--
-41.1 到 -39.4
°C
ASTM D7028-- 6-40.0
°C
ISO 11357-2维卡软化温度79.0
°C
ISO 306/B50熔融温度-- 6
143
°C
ISO 11357-3--140 到 145
°C
ASTM D3418线形热膨胀系数 - 流动23°C
1.3E-4 到 1.9E-4
cm/cm/°C
ASTM D696--1.6E-4
cm/cm/°C
ISO 11359-2比热745 到 958
J/kg/°C
DSC导热系数0.14 到 0.18
W/m/K
ASTM D433RTI Elec130
°C
UL 746BRTI Imp130
°C
UL 746BRTI130
°C
UL 746B电气性能额定值
单位制
测试方法
表面电阻率 (23°C)5.1E+11 到 5.3E+11
ohms
ASTM D257体积电阻率20°C 7
2.0E+14
ohms·cm
ASTM D257--2.0E+14
ohms·cm
IEC 60093介电强度 (23°C)51 到 59
kV/mm
ASTM D149介电常数1 kHz
3.50 到 10.6
ASTM D150100 Hz
11.0
IEC 602501 MHz
7.00
IEC 60250耗散因数
100 kHz
0.020 到 0.21
ASTM D150100 Hz
0.23
IEC 602501 MHz
0.052
IEC 60250可燃性
额定值
单位制
测试方法
可燃性等级IEC 60695-11-10, -200.8 mm
V-0
1.5 mm
V-0
极限氧指数
-- 4
42
%
ASTM D2863--43
%
ISO 4589-2光学性能额定值
单位制
测试方法
折射率 81.410
ASTM D542充模分析
额定值
单位制
测试方法
熔体粘度 (230°C, 100 sec^-1)2200 到 2700
Pa·s
ASTM D3835补充信息额定值
单位制
测试方法
热分解温度TGAin air, 1% wt. loss
375
°C
in nitrogen, 1% wt. loss
410
°C