库存华南库EAA 5990 陶氏/盛禧奥/斯泰隆

EAA 5990物性表物理性能测试条件测试方法测试结果单位熔体质量流动速率125°C/2.16kg2ASTMD1238,ISO113365g/10min190°C/2.16kg3ASTMD1238,ISO11331300g/10min共聚单体含量4内部方法20.0%机械性能测试条件测试方法测试结果单位拉伸模量-2%正割模压成型ASTMD638,ISO527-222.1Mpa抗张强度断裂,模压成型ASTMD638,ISO527-26.21Mpa伸长率断裂,模压成型ASTMD638,ISO527-2350%拉伸模量-2% SecantCompression MoldedMPaASTM D-63822.1Compression MoldedMPaISO 527-222.1拉伸断裂强度Compression MoldedMPaASTM D-6386.21Compression MoldedMPaISO 527-26.21拉伸断裂伸长率Compression Molded%ASTM D-638350Compression Molded%ISO 527-2350热性能测试条件测试方法测试结果单位维卡软化点℃ASTM D-1525℃ISO 306熔融温度℃Internal Method75维卡软化温度ASTMD1525,ISO30640.0°C溶融温度（DSC）内部方法75.0°C基本性能测试条件测试方法测试结果单位熔融指数125℃/2.16kgg/10minASTM D-1238125℃/2.16kgg/10minISO 1133190℃/2.16kgg/10minASTM D-12381300190℃/2.16kgg/10minISO 11331300单体含量%Internal Method