EAA 3004 美国盛禧奥(斯泰隆)

EAA 美国盛禧奥(斯泰隆) 3004物性表物理性能测试条件测试方法测试结果单位密度 / 比重g/cm³ASTM D-7920.938g/cm³ISO 11830.938ASTMD792,ISO11830.938g/cm³熔体质量流动速率2190°C/2.16kgASTMD1238,ISO11338.5g/10min共聚单体含量39.7%机械性能测试条件测试方法测试结果单位抗张强度屈服,模压成型ASTMD638,ISO527-27.93Mpa断裂,模压成型ASTMD638,ISO527-217.6Mpa伸长率断裂,模压成型ASTMD638,ISO527-2600%拉伸屈服强度Compression MoldedMPaASTM D-6387.93Compression MoldedMPaISO 527-27.93拉伸断裂强度Compression MoldedMPaASTM D-63817.6Compression MoldedMPaISO 527-217.6拉伸断裂伸长率Compression Molded%ASTM D-638600Compression Molded%ISO 527-2600热性能测试条件测试方法测试结果单位维卡软化温度ASTMD1525,ISO30681.1°C溶融温度（DSC）内部方法98.0°C维卡软化点℃ASTM D-152581.1℃ISO 30681.1加工性能测试条件测试方法测试结果单位熔体温度℃260-290基本性能测试条件测试方法测试结果单位熔融指数190℃/2.16kgg/10minASTM D-12388.5190℃/2.16kgg/10minISO 11338.5单体含量%9.7